Modifikasi Elektroda Perak Dengan Silika Gel-Ekstrak Daun Maja (Aegle Marmelos) Sebagai Biosensor Urea

Triana, Yunita (2015) Modifikasi Elektroda Perak Dengan Silika Gel-Ekstrak Daun Maja (Aegle Marmelos) Sebagai Biosensor Urea. Undergraduate thesis, Institut Technology Sepuluh Nopember.

[thumbnail of 1413201009-Undergraduate Thesis.pdf]
Preview
Text
1413201009-Undergraduate Thesis.pdf - Published Version

Download (1MB) | Preview

Abstract

Pada penelitian ini elektroda perak termodifikasi silika gel-ekstrak daun maja (Aegle marmelos) digunakan sebagai elektroda kerja alternatif untuk mendeteksi urea secara elektrokimia. Perkembangan elektroda termodifikasi silika gel untuk penentuan urea yang telah dilakukan pada penelitian sebelumnya menggunakan urease sehingga dibuat pengembangan elektroda alternatif dari ekstrak daun maja. Daun maja diekstraksi menggunakan etanol sehingga diperoleh ekstrak daun maja dan disimpan pada suhu -110C. Elektroda perak termodifikasi dipreparasi dalam bentuk pasta silika gel dan ekstrak daun maja pada permukaan elektroda perak. Elektroda memberikan respon terbaik dengan perbandingan komposisi pasta silika gel dan parafin yaitu 3 : 2 dengan berat total 0,05 gram. Sedangkan optimasi ekstrak daun maja pada kondisi optimum komposisi silika gel dan parafin sebanyak 0,03 gram. Kondisi larutan diatur tingkat keasamannya pada range pH 1, 7 dan 13 untuk menentukan pH optimum. Pada pH 1 dan 7 pendeteksian urea terganggu oleh asam askorbat dan glukosa. Pengukuran optimum didapatkan pada kondisi pH 13 dimana deteksi urea tidak terganggu asam askorbat dan glukosa. Elektroda menunjukkan kenaikan sinyal arus seiring kenaikan konsentrasi urea. Variasi konsentrasi urea (0-7 μM) untuk menentukan limit deteksi dan sensitivitas. Sinyal arus katodik elektroda perak termodifikasi silika gel dan ekstrak daun maja pada potensial 0,4 V memiliki sensitivitas dan limit deteksi yaitu 19,7813 μAμM-1mm-2 dan 2,2993 μM. Sinyal arus anodik elektroda perak termodifikasi silika gel dan ekstrak daun maja pada potensial 0,625 V memiliki sensitivitas dan limit deteksi yaitu 38,1774 μAμM-1mm-2 dan 5,1654 μM. Uji repeatibilitas dan reproduksibilitas dilakukan untuk menentukan presisi dan akurasi dari elektroda perak termodifikasi silika gel-ekstrak daun maja.
=================================================================================================
Silica gel-maja leaf extract (Aegle marmelos) modified silver electrode has been studied as an alternative urea biosensor electrochemically. Previous other works showed that determination of urea mainly used urease as an active material. In this work, we used maja leaf extract instead of urease. Maja leaf was extracted using ethanol and stored at -11oC. Maja leaf extract, silica gel and parafin was mixed until homogen, then attached on the end of the silver wire which was tightly covered by glass tube to have silica gel-maja leaf extract modified silver electrode. Electrodes provide the best response to the paste composition ratio of silica gel and paraffin is 3: 2 with the total weight 0,05 gram, while optimum composition for the maja leaf extract is 0,03 gram. Electrode showed that the current signal rise following the increase in the concentration of urea (0-7 μM) Measurement of urea was performed in varied pH (1, 7 and 13) using cyclic voltammetry. pH 1 and 7 showed that ascorbic acid and glucose interfered the urea detection. pH 13 showed that no interference of ascorbic acid and glucose during the urea measurement. Cathodic electrode current signal silver modified silica gel-maja leaf extract in the potential of 0.4 V showed that the sensitivity and the detection limit is 19,7813 μAμM-1mm-2 and 2,2993 μM. Anodic electrode current signal silver modified silica gel and maja leaf extract in the potential of 0.625 V showed that the sensitivity and the detection limit is 38,1774 μAμM-1mm-2 and 5,1654 μM. In the last work, repeatibilitas and reproducibility of test performed to determine the precision and accuracy of the electrode.

Item Type: Thesis (Undergraduate)
Additional Information: RTKi 541.372 4 Tri m
Uncontrolled Keywords: silika gel, ekstrak daun maja, urea, voltammetri siklis
Subjects: T Technology > TP Chemical technology > TP255 Electrochemistry, Industrial.
Divisions: Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Mr. Tondo Indra Nyata
Date Deposited: 18 Dec 2018 03:04
Last Modified: 18 Dec 2018 03:04
URI: http://repository.its.ac.id/id/eprint/60095

Actions (login required)

View Item View Item