Studi Eksperimental dan Analisa Pengaruh Sinar Matahari Terhadap Laju Keausan Material Ethylene Propylene Diene Monomers (EPDM) pada Wiper Blade

Fu'adi, Muzayin Ahmad (2019) Studi Eksperimental dan Analisa Pengaruh Sinar Matahari Terhadap Laju Keausan Material Ethylene Propylene Diene Monomers (EPDM) pada Wiper Blade. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2114100087-Undergraduate_Theses.pdf]
Preview
Text
2114100087-Undergraduate_Theses.pdf

Download (2MB) | Preview

Abstract

Wiper merupakan komponen yang sangat penting dan erat hubungannya dengan keselamatan pengendara terutama pada saat turun hujan karena wiper blade akan menyapu air hujan yang jatuh ke kaca mobil. Pada saat wiper blade bekerja akan terjadi gesekan pada material wiper blade dengan kaca yang dapat mengakibatkan adanya keausan pada material wiper yang biasanya terbuat dari rubber dengan jenis Ethylene Propylene Diene Monomers (EPDM).
Penelitian untuk mengetahui pengaruh sinar matahari terhadap laju keausan (wear rate) dan life time dari material wiper blade dilakukan menggunakan tribometer pin on disk dengan variasi material pada pin berupa material Ethylene Propylene Diene Monomers (EPDM) dan Nitrile Rubber (NBR) dimana pada masing-masing material disinari matahari dengan lama waktu yang berbeda. Kecepatan putar yang digunakan adalah 31,3 rpm dengan pembebanan 14,71 N dan panjang lintasan 1000 m.
Berdasarkan penelitian yang telah dilakukan, dapat diketahui bahwa nilai specific wear rate akan semakin besar seiring semakin lama material terkena matahari. Life time terbaik untuk material Ethylene Propylene Diene Monomers (EPDM) adalah sekitar 3,7 tahun dan life time terbaik untuk material Nitrile Rubber (NBR) adalah sekitar 5,5 tahun sehingga dapat dijadikan sebagai material pengganti.
================================================================================================
The wiper is a very important component and is closely related to the safety of the driver, especially when it rains because the wiper blade will sweep away the rain water that fall into the windshield. When the wiper blade which is usually made of Ethylene Propylene Diene Monomers (EPDM) works, there will be a friction on the glass which causes wear on the wiper material.
This study aims to determine the effect of sunlight on the wear rate and life time of the wiper blade material and to seek the alternative material that can be used as a substitute for Ethylene Propylene Diene Monomers (EPDM) material. The test is carried out using tribometer pin on disk type with material variations on the pin in the form of Ethylene Propylene Diene Monomers (EPDM) material and Nitrile Rubber (NBR) Ethylene Propylene Diene Monomers (EPDM) wherein each sun is irradiated at different lengths of time. The rotational speed used is 31,3 rpm with a load of 14.71 N and a track length of 1000 m.
The study showed that the specific wear rate will be greater as the material is exposed to the sun. The best life time for Ethylene Propylene Diene Monomers material is 3,7 years and the best life time for Nitrile Rubber (NBR) material is 5,5 years so that it can be used as a substitute material.

Item Type: Thesis (Undergraduate)
Additional Information: RSM 629.266 Fua s-1 2019
Uncontrolled Keywords: wiper, wiper blade, EPDM, NBR, wear rate, life time
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User: Muzayin Ahmad Fuadi
Date Deposited: 31 Jul 2021 09:32
Last Modified: 31 Jul 2021 09:32
URI: http://repository.its.ac.id/id/eprint/61084

Actions (login required)

View Item View Item