Pengaruh variasi heat input pengelasan SMAW pada SS400 terhadap sifat mekanik impak temperatur, kekerasan dan struktur mikro

Jaya, Dendy Dwi Rohma Prahara (2018) Pengaruh variasi heat input pengelasan SMAW pada SS400 terhadap sifat mekanik impak temperatur, kekerasan dan struktur mikro. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 10211500000089_Non_Degree.pdf]
Preview
Text
10211500000089_Non_Degree.pdf

Download (5MB) | Preview

Abstract

Dalam dunia industry kapal banyak digunakan material baja untuk kebutuhan konstruksi body kapal. Salah satu pilihan untuk menyambungkan 2 baja atau lebih menjadi satu kesatuan adalah dengan pengelasan. Prosedur pengelasan yang salah akan berpengaruh pada penurunan kualitas barang produksi seperti kekuatan sambungan las dan ketangguhan las. Sehingga salah prosedur pengelasan akan berakibat fatal.
Pada pengujian ini menggunakan plat baja SS400 dengan kadar C sebesar 0.12%. Disambungkan dengan metode pengelasan SMAW. Dalam hal ini menggunakan variasi heat input. Tujuan dari dilakukannya variasi heat input tersebut yaitu untuk mengetahui hasil terbaik dari variasi heat input, pengujian dalam penelitian ini meliputi Pengujian Impak Temperatur, Uji Struktur Mikro dan Kekerasan.
Dari hasil penelitian menunjukkan bahwa pengelasan dengan heat input lebih besar menjadi pilihan yang terbaik untuk menerima gaya impak. Hal ini dikarenakan heat input besar yang diterima Weld Metal dan HAZ membuat hasil lasan menjadi ulet/ tangguh.
================================================================================================
In the naval industrial world widely used steel materials for the needs of the construction of the naval body. One of the options to connect 2 or more steel into one unit is by welding. The wrong welding procedures will affect the quality of goods production decreased as strength and toughness of weld weld connection. So wrong welding procedures will be fatal.
On testing this using SS400 steel plate with C of 0.12%. Connected with the method of welding SMAW. In this case use a variety of heat input. Purpose of doing variations of the heat input i.e. to know the best results from the variation of the heat input, testing in this study include Testing the impact Test temperature, Microstructure and Violence.
Results showed that of the welding amperage with 120 being the best option to receive style impact. This is due to the large heat input Weld Metal and HAZ accepted making the results of weld being resilient/tough.

Item Type: Thesis (Undergraduate)
Additional Information: RSMI 671.52 Jay p-1 2019
Uncontrolled Keywords: Steel, Las SMAW, Welding, Amperage, Heat Input, Impact Test, Micro Test, Hardness Test
Subjects: T Technology > TS Manufactures > TS227 Welding.
Divisions: Faculty of Vocational > Mechanical Industrial Engineering
Depositing User: Dendy Dwi Rohma Prahara Jaya
Date Deposited: 08 Apr 2022 05:24
Last Modified: 08 Apr 2022 05:24
URI: http://repository.its.ac.id/id/eprint/62314