Studi pengaruh ketahanan stress corrosion cracking (SCC) pada pengelasan stainless steel 304 dengan metode u-bend stress pada tangki ruang muat chemical tanker

Pratiwi, Intan (2015) Studi pengaruh ketahanan stress corrosion cracking (SCC) pada pengelasan stainless steel 304 dengan metode u-bend stress pada tangki ruang muat chemical tanker. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
4111100095-Undergraduate_Thesis.pdf

Download (4MB) | Preview

Abstract

Baja Tahan Karat (Stainless Steel) merupakan suatu baja yang tahan terhadap korosi. Stainless Steel biasa digunakan pada peralatan maupun struktur untuk konstruksi. Dalam industri perkapalan sendiri Stainless Steel yang banyak digunakan adalah Stainless Steel jenis 304. Salah satu korosi yang mungkin terjadi adalah Stress Corrosion Cracking (SCC). Korosi ini timbul karena adanya kerentanan paduan, lingkungan ekstrim, dan tegangan sisa. Penelitian ini ditujukan untuk mengetahui ketahanan akan SCC pada salah satu pengelasan material Stainless Steel yaitu Stainless Steel jenis 304 dengan menggunakan metode U-bend Stress. Pengujian dilakukan dengan membandingkan timbulnya retak sebagai identifikasi terjadinya SCC pada base metal dan weld metal. Dimana pengujian ini mengacu pada ASTM G-30 (Making and Using U-bend Stress Corrosion Cracking), ASTM G-36 (Practice for Performing Stress Corrosion Cracking Test in a Boiling Magnesium Chloride Solution), dan ASTM G-58 (Preparation of Stress Corrosion Cracking Test Specimens For Weldments). Dari hasil pengujian yang telah divariasikan dengan lamanya waktu pengujian, dapat diketahui bahwa panjang retak maksimum pada base metal adalah 0.445 mm, sedangkan panjang retak maksimum pada weld metal yaitu 0.468 mm. Kemudian untuk jumlah retak maksimum yang timbul pada base metal adalah 3 retak, sedangkan jumlah retak maksimum yang timbul pada weld metal yaitu 5 retak. Dengan adanya retak-retak yang timbul maka dapat disimpulkan bahwa pengujian Stress Corrosion Cracking (SCC) dengan metode ini mampu diterapkan pada Stainless Steel jenis 304, sehingga dapat diketahui jumlah retak dan panjang retak yang terjadi. =============================================================================================== Stainless Steel is a corrosion resistant material. Stainless Steel is used on equipment and structures of construction. In the ship building industry, stainless steel that widely used is type 304. One of corrosion that may occur is stress corrosion cracking (SCC). This corrosion arises because of the vulnerability of the alloy, extreme environments, and residual stress. The purpose of this research is to study the resistance of SCC on welding one of the stainless steel material which is stainless steel type 304 using U-bend Stress Method. This test is done with comparing SCC showing on base metal and weld metal. It’s based on ASTM G-30 (Making and Using U-bend Stress Corrosion Cracking), ASTM G-36 (Practice for Performing Stress Corrosion Cracking Test in a Boiling Magnesium Chloride Solution), and ASTM G-58 (Preparation of Stress Corrosion Cracking Test Specimens For Weldments). From the test result which is variated with the testing duration, it showed in the interval time 0-24 hours with HCl the lenght of maximum crack in base metal is 0.445 mm. Then, the lenght of maximum crack in weld metal is 0.468 mm. The number or crack in base metal is three crack, and for the number or crack in weld metal is five crack. The result of the test can be conclused that the U-bend Test Method can be used on Stainless Steel 304, so can be known the number of cracks and the crack length.

Item Type: Thesis (Undergraduate)
Additional Information: RSPe 112 23 Pra s
Uncontrolled Keywords: Stainless Steel; U-bend; SCC; HCl; retak
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.75 Corrosion-resistant materials
Divisions: Faculty of Marine Technology (MARTECH) > Naval Architecture and Shipbuilding Engineering > 36202-(S1) Undergraduate Thesis
Depositing User: - Taufiq Rahmanu
Date Deposited: 09 Oct 2019 02:43
Last Modified: 09 Oct 2019 02:43
URI: https://repository.its.ac.id/id/eprint/71061

Actions (login required)

View Item View Item