Baharuddin, Azhar Basyir (2016) Analisa Kegagalan Rocker Arm Pada Vertical Roller Mill Di Coal Mill Tuban 1 Pt. Semen Indonesia. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2712100134-undergraduate-theses.pdf - Published Version Download (4MB) | Preview |
Abstract
Vertical Roller Mill memiliki peranan penting pada Industri
Semen sebagai Penghancur batu bara yang digunakan sebagai
bahan bakar pembuatan semen. Pada Vertical Roller mill sering
sekali terjadi kegagalan terutama pada bagian Rocker Arm. Rocker
arm memiliki kegunaan sebagai tempat menahan beban putaran
dari komponen penggerak Vertical Roller Mill. Dalam penelitian
ini dilakukan untuk menganalisa penyebab terjadinya kegagalan
pada Rocker Arm. Pengujian yang dilakukan untuk menganalisa
material ini adalah, uji komposisi, metalografi, hardness, SEM,dan
uji titik kritis tegangan dengan menggunakan software inventor.
Dari hasil uji komposisi didapatkan material rocker arm memiliki
perbandingan komposisi yang sama dengan standar DIN 1681 GS
60 yaitu cast steel.Kemudian dari uji kekerasan ini diperoleh data
rata-rata nilai kekerasan pada daerah yang mengalami kegagalan
sebesar 256 HB, dan pada daerah yang jauh dari kegagalan sebesar
206 HB.Hasil dari permodelan diperoleh tegangan yang tinggi
pada lingkaran rocker arm yang mengalami kegagalan.Analisa
struktur mikro dan makro pada komponen rocker arm ini dan
analisa karakterisasi material dari SEM menunjukkan pola patah
lelah getas akibat tingginya tegangan yang berulang-ulang pada
daerah rocker arm.
=======================================================
Vertical Roller Mill has an important role in the Cement
Industry as crusher of coal to be used as fuel in cement process. At
Vertical Roller mill failure often occurs, especially on the Rocker
Arm. Rocker arm has function as structure to hold bearing rotation
load of drive components Vertical Roller Mill. In this study
conducted to analyze the causes of failure in the Rocker Arm. Tests
were carried out to analyze this material are ,composition test,
metallographic, hardness, SEM, and critical stress test by using
software inventor. From the test results obtained material
composition ratio rocker arm has the same composition with the
standard DIN 1681 GS 60 is cast steel.From hardness test data
showed the average value of hardness in area that near the failure
is 256 HB, and in area far from failure is 206 HB.Result of
modeling obtained a high stress concentration in the circle of
failure rocker arm.Micro and macro structures analysis on the
rocker arm component and material characterization of SEM
showed fatigue brittle fracture due to high stress applied repeatedly
on the rocker arm area.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Additional Information: | RSMt 620.112 6 Bah a |
| Uncontrolled Keywords: | Rocker Arm, Vertical Roller Mill,Cast Steel, Patah Lelah Getas, Hardness. |
| Subjects: | T Technology > TN Mining engineering. Metallurgy > TN690 Metallography. Physical metallurgy |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | EKO BUDI RAHARJO |
| Date Deposited: | 28 Oct 2019 08:41 |
| Last Modified: | 28 Oct 2019 08:41 |
| URI: | http://repository.its.ac.id/id/eprint/71460 |
Actions (login required)
 |
View Item |