Fabrikasi Pandu Gelombang X Cross Dengan Film Sno2 Nano Sebagai Pembagi Daya Lucky Putri Rahayu

Rahayu, Lucky Putri (2016) Fabrikasi Pandu Gelombang X Cross Dengan Film Sno2 Nano Sebagai Pembagi Daya Lucky Putri Rahayu. Masters thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1114201020-master-theses.pdf]
Preview
Text
1114201020-master-theses.pdf - Published Version

Download (3MB) | Preview

Abstract

Salah satu aplikasi pandu gelombang slab yaitu sebagai pembagi daya.
Struktur pandu gelombang X cross memiliki empat port dimana satu port sebagai
input dan tiga port lainnya sebagai output. Fabrikasi pandu gelombang Straight
dan X Cross yang telah dilakukan pada penelitian ini terdiri dari substrat akrilik,
film SnO2 dan cover MMA. Pola Straight dan X Cross dibuat menggunakan
software Corel draw X6 dan kemudian di grafir diatas substrat akrilik dengan
variasi panjang 1 cm, 1,5 cm dan 2 cm pada Straight dan sudut percabangan pada
X Cross yaitu 15°, 30°, 45° dan 60°. Setelah itu dilakukan variasi tegangan pada
pandu gelombang X Cross yaitu 5,4 volt, 6,4 volt dan 7,4 volt. Analisa distribusi
intensitas diperoleh dari gambar cross section yang kemudian diolah
menggunakan software ImageJ. Dari hasil didapatkan nilai propagation loss pada
pandu gelombang Straight dengan panjang 1 cm yaitu 2,784 %, 1,5 cm yaitu
7,927 % dan 2 cm yaitu 18,352 %. Pada Pandu gelombang X Cross sudut 15°
didapatkan output tertinggi terletak pada port yang segaris sehingga jumlah daya
yang terpandu menjadi lebih besar. Pada Pandu gelombang X Cross sudut 30°, 45°
dan 60° terjadi pembelokan cahaya, hal tersebut dapat diindikasikan karena sifat
kenon-linieritas dari bahan SnO2. Dari hasil karakterisasi pandu gelombang X
Cross dengan variasi tegangan tiap sudut didapatkan perubahan prosentase
terhadap input untuk tiap-tiap port, hal tersebut juga dapat dikarenakan sifat non
linieritas dari bahan SnO2
===========================================================
One application of slab waveguide is power divider. X cross waveguide
structure there are four ports where one input port and three possible outputs.
Straight and X Cross waveguide fabrication that has been done in this study
consisted of acrylic substrates, SnO2 as film and cover MMA. Straight and X
Cross pattern created using Corel Draw X6 software and then engraved on the
substrate of acrylic with a variation length of 1 cm, 1.5 cm and 2 cm on the
Straight and angle branching on the X Cross are 15 °, 30 °, 45 ° and 60 °. Once it
is done on X Cross waveguide voltage variation are 5.4 volts, 6.4 volts and 7.4
volts. Analysis distribution of intensity obtained from cross-section images and
then process used ImageJ software. From the results obtained value loss on
Straight waveguide length 1 cm is 2.784 %, 1.5 cm is 7.927 % and 2 cm is 18.352
%. In X Cross waveguides of angle 15° obtained the highest output is located on
the port of slightly so that the amount of power is guided to be larger. In X Cross
waveguides of angle 30°, 45° and 60° is occurred deflection of lights and it is
indicated of characteristic non linearity materials SnO2. From the results of the
characterization of waveguides X Cross with voltage variation change of the input
obtained for each port, it can also indicated of characteristic non linearity
materials SnO2.

Item Type: Thesis (Masters)
Additional Information: RTFi 621.312 44 Rah f
Uncontrolled Keywords: Pandu Gelombang, X Cross, Straight, Pembagi Daya, SnO2 Nano
Subjects: T Technology > TC Hydraulic engineering. Ocean engineering
T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK1056 Solar powerplants
T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK1087 Photovoltaic power generation
Divisions: Faculty of Natural Science > Physics > 45101-(S2) Master Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 20 Nov 2019 02:01
Last Modified: 20 Nov 2019 02:01