Studi Eksperimen Dan Analisa Keausan Journal Brearing Dengan Lapisan Pasta Pada Rotary Valve Mesin Pembuat Pasta

Inayah, Nazidatul (2015) Studi Eksperimen Dan Analisa Keausan Journal Brearing Dengan Lapisan Pasta Pada Rotary Valve Mesin Pembuat Pasta. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2110100701-Undergraduate-Thesis.pdf

Download (3MB) | Preview

Abstract

Setiap peralatan yang bergerak selalu mengalami kerusakan. Hal ini dikarenakan adanya dua benda yang saling berkontak atau bergesekan. Permasalahan yang dialami oleh salah satu industri ini adalah sering terjadi kebocoran pada mesin pembuatan pasta yaitu pada bagian rotary valve, dimana pada rotary valve ini terjadi kontak antara material polyoxymethylene (POM) dan SS316. Oleh karena itu perlu adanya sebuah penelitian untuk mengetahui specific wear rate material polyoxymethylene (POM) dengan hadirnya pasta. Langkah-langkah penelitian yang dilakukan adalah sebelum dilakukan pengujian pada mesin tribometer, terlebih dahulu spesimen uji direndam dengan menggunakan pasta gigi pepsodent whitening untuk mengetahui pengaruh pasta terhadap material uji. Setelah direndam, spesimen uji ditimbang dengan menggunakan timbangan digital. Setelah itu dilakukan pengujian dengan menggunakan mesin tribometer dengan menggunakn pembebanan konstan yaitu 8 kg dan 3 variasi kecepatan yaitu pada speed control 50 (38,7 rpm), 60 (44,4 rpm) dan 70 (52,3 rpm). Pengujian dilakukan dengan menggunakan pelumas berupa pasta pepsodent whitening. Sebelum pengujian dimulai, dilakukan penimbangan massa awal spesimen uji yaitu massa setelah spesimen uji direndam dengan pasta gigi dan kalibrasi alat yaitu speed control dan load. Pengulangan dilakukan sebanyak 3 kali sesuai dengan speed control yang ditetapkan. xviii Setelah pengujian dilakukan foto mikro dan analisa struktur permukaan. Hasil dari pengujian diatas didapatkan material rekomendasi yang memiliki nilai specific wear rate lebih baik dibandingkan dengan material polyoxymethylene (POM), yaitu polytetrafluoroethylene (PTFE). Dimana nilai specific wear rate polytetrafluoroethylene (PTFE) jauh lebih baik dibandingkan dengan material polyoxymethylene (POM). Yaitu yaitu pada saat kecepatan 0,04 m/s 3x lebih baik, pada kecepatan 0,046 m/s 2x lebih baik, dan pada kecepatan 0,054 m/s 1x lebih baik. Nilai specific wear rate ini juga berpengaruh terhadap umur hidup (life time) material. Yaitu pada saat kecepatan 0,04 m/s 2x lebih baik, pada kecepatan 0,046 m/s 1x lebih baik, dana pada kecepatan 0,054 m/s 1x lebih baik. =============================================================================================== Any equipment that moves always damaged. This is because the two objects come into contact or rub against each other. Problems experienced by one industry are often leak on machine of pasta makers that is on the rotary valve, wherein the rotary valve is in contact between the material polyoxymethylene (POM) and SS316. Threfore, need a experiment to determine the specific wear rate material polyoxymethylene (POM) with the presence of pasta. Steps before the research is conducted testing on Tribometer machine, first test specimen is immersed by using Pepsodent toothpaste whitening pastes to determine the effect of the test material. After soaking, the test specimens were weighed using a digital scale. After it was examined by using a machine Tribometer with constant loading is 8 kg and 3 variations in speed control the speed of which 50 (38.7 rpm), 60 (44.4 rpm) and 70 (52.3 rpm). Tests carried out using a lubricant such as Pepsodent whitening paste. Before the test begins, weighing is done the initial mass is the mass of the test specimen after the test specimens soaked with toothpaste and calibration tools that speed and load control. Repetition done 3 times in accorance with the speed control set. After testing done micro photo and surface structure analysis. Results of tests on material obtained which has a value of specific recommendations wear rate is better than the material POM, which is polytetrafluoroethylene(PTFE). Where the value xx of specific wear rate of polytetrafluoroethylene (PTFE) is much better than the material polyoxymethylene (POM). Namely that when the speed of 0,04 m/s 3x better, at a speed of 0,046 m/s 2x better, and at a speed of 0,054 m/s 1x better. The value of specific wear rate also affects the lifetime of the material. Namely when the speed of 0,04 m/s 2x better, at a speed of 0,046 m/s 1x better, at a speed of 0,054 m/s 1xbetter.

Item Type: Thesis (Undergraduate)
Additional Information: RSM 621.815 Ina s
Uncontrolled Keywords: Polyoxymethylene (POM), Polytetrafluoroethylene (PTFE), lubricated, wear rate
Subjects: T Technology > TJ Mechanical engineering and machinery > TJ230 Machine design
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User: Mr. Marsudiyana -
Date Deposited: 12 Dec 2019 07:04
Last Modified: 12 Dec 2019 07:04
URI: https://repository.its.ac.id/id/eprint/72344

Actions (login required)

View Item View Item