Pengaruh Jumlah Layer Aluminium Terhadap Ketahanan Korosi Dan Ketahanan Aus Pada Pelapisan Baja Api 5l Grade B Menggunakan Metode Wire Arc Spray

Imanullah, Rangga Al Gifary (2016) Pengaruh Jumlah Layer Aluminium Terhadap Ketahanan Korosi Dan Ketahanan Aus Pada Pelapisan Baja Api 5l Grade B Menggunakan Metode Wire Arc Spray. Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[thumbnail of 2712100107-undergraduate-theses-.pdf]
Preview
Text
2712100107-undergraduate-theses-.pdf - Published Version

Download (2MB) | Preview

Abstract

Korosi adalah masalah utama penyebab terjadinya
kegagalan pada material terutama pada pipeline yang
merupakan peralatan untuk menyalurkan minyak atau gas bumi
reservoir. Untuk mencegah atau mengurangi terjadinya korosi
dilakukan proteksi atau perlindungan pada pipeline,
perlindungan yang paling umum dilakukan adalah melapisi
dengan lapisan proteksi atau coating. Penelitian ini
menggunakan coating dengan metode wire arc spray dengan
variasi jumlah lapisan pada coating sebanyak 6 layer, 8 layer,
dan 10 layer. Material coating yang digunakan adalah
Aluminium wire 99,8% untuk melapisi substrat baja API 5L
Grade B pada lingkungan NaCl 3,5%. Kemudian dilakukan
pengukuran ketebalan, pengujian daya lekat, pengujian laju
korosi, pengujian EDX, dan pengujian laju keausan terhadap
spesimen. Ketebalan yang tertinggi didapat pada variabel 10
layer dengan ketebalan 1323,67 μm, daya lekat tertinggi didapat
pada variabel 6 layer dengan nilai 38,82 MPa, ketahanan korosi
tertinggi didapat pada jumlah layer 10 dengan nilai 0,019102
mm/year, dan ketahanan aus tertinggi terdapat pada spesimen
dengan variabel 6 layer dengan nilai sebesar 5,21 mg/cm2/jam.
Dalam penelitian ini, didapatkan variabel 6 layer yang paling
efektif dan ekonomis untuk diaplikasikan karena memiliki
viii
ketahanan korosi yang cukup untuk mencegah terbentuknya
produk korosi dan memiliki ketahanan aus yang tertinggi dengan
harga yang lebih murah dibandingkan variabel lainnya.
==========================================================
Corrosion is a major problem the cause of the failure on
the material, especially in the pipeline which is the equipment to
deliver oil or gas from the reservoir. To prevent or reduce the
occurrence of corrosion, some kind of protection is undego in the
pipeline, the protection of the most common is to coat with a
protective layer or coating. This research is using wire arc spray
coating method with amount of coating layer as much as 6
layers, 8 layers and 10 layers as the variations. Coating material
used is aluminum wire 99.8% Al for the coating of steel
substrates API 5L Grade B in the environment of NaCl 3.5%.
Then the measurement of thickness, adhesion testing, the testing
of corrosion rate, EDX testing and wear rate testing were
performed on specimens. Based on the results, the highest
thickness obtained on the variable 10 amount of layer with a
thickness of 1323.67 μm, the highest adhesion strength is
obtained in the variable 6 amount of layer with a value of 38.82
MPa, the highest corrosion resistance is obtained on the number
of layers 10 with a value of 0.019102 mm/year , and wear
resistance is highest in the specimen with variable 6 amount of
layer with a value of 5.21 mg/cm2/hour. In this research,it can be
concluded that 6 layers variable suit the requirement the best
because of its corrosion resistance that is sufficient to prevent the
x
corrosion to occur and it provides the highest wear resistance
with lower cost compared to another variables.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.112 23 Ima p-1
Uncontrolled Keywords: Coating, Daya Lekat, Laju Aus, Ketahanan Korosi, Ketahanan Aus
Subjects: T Technology > TN Mining engineering. Metallurgy > TN690 Metallography. Physical metallurgy
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 23 Dec 2019 07:46
Last Modified: 23 Dec 2019 07:46
URI: http://repository.its.ac.id/id/eprint/72466

Actions (login required)

View Item View Item