Pengaruh Temperatur Warm Kompaksi Dan Tekanan Kompaksi Terhadap Sifat Mekanik Komposit Cu-10%Sn + 0,6% Zinc Stearate Sebagai Material Peluru Frangible Mahardika Kurnia Dewantara

Dewantara, Mahardika Kurnia (2016) Pengaruh Temperatur Warm Kompaksi Dan Tekanan Kompaksi Terhadap Sifat Mekanik Komposit Cu-10%Sn + 0,6% Zinc Stearate Sebagai Material Peluru Frangible Mahardika Kurnia Dewantara. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2712100057-Undergraduate_Thesis.pdf - Published Version

Download (3MB) | Preview

Abstract

Peluru frangible adalah peluru yang didesain untuk hancur saat mengenai target yang keras. Pada umumnya proses pembuatan peluru frangible dilakukan menggunakan metode cold compaction. Namun cold compaction memiliki beberapa tahapan yang memerlukan waktu yang cukup lama. Metode warm kompaksi ini menggabung tahapan kompaksi dan sintering menjadi satu tahap sehingga mengurangi waktu produksi. dalam penelitian ini dilakukan dengan proses (1) Wet Mixing Cu- 10%wtSn + 0,6%wt zinc stearate, (2) kompaksi dengan variasi temperatur 100, dan 200OC dan tekanan 300, 400, 500 600 Mpa dan waktu tahan 10 menit. Berdasarkan pengujian densitas didapatkan densitas terbesar dan porositas terendah pada temperatur 100OC dan tekanan 500 MPa sebesar 8.144g/cm3 dan 6.925%. Berdasarkan pengujian kekrasan nilai tertinggi didapatkan pada temperatur 100OC dan tekanan 500 MPa sebesar 76.30 HV. Hasil Kekuatan tekan terbesar tercatat pada temperatur 100OC dan tekanan 500 MPa sebesar 315.714 MPa. Berdasarkan hasil uji XRD didapatkan fasa yang terbentuk adalah Cu, Sn, Cu3Sn, dan Cu6Sn5. ================================================================= Frangible bullet is a bullet that designed to be shattered when it smash a hard target. Generally frangible bullet is made from cold compaction method. But cold compaction has some steps makes this method is time consuming. Warm compaction method unite compaction method and sintering method in one time. Warm compaction can reduce the production time. The processes in this research are (1) Wet mixing the powders (Cu10%Sn + 0,6% Zinc stearate) and adding an ethanol to reduce a potential to an oxidation reaction. (2) compaction with temperature variation 100OC and 200OC and pressure variation 300, 400, 500, 600 MPa with 10 minutes holding time. As the results Tests, the highest value of density, hardness, compression, and the lowest value of porosity noted 8.144g/cm3, 76.30 HV, 315.714 MPa, and 6.925%. XRD test shows the formation of Cu, Cu6Sn5, Cu3Sn, and Sn. SEM – EDX result shows the same phase in the Cu10wt%Sn + 0,6% Zinc stearate composite sample.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 671.374 Dew p-1
Uncontrolled Keywords: warm kompaksi, sifat mekanik, metalurgi serbuk
Subjects: T Technology > TN Mining engineering. Metallurgy > TN690 Metallography. Physical metallurgy
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 08 Jan 2020 03:43
Last Modified: 08 Jan 2020 03:43
URI: https://repository.its.ac.id/id/eprint/72593

Actions (login required)

View Item View Item