Rancang Bangun Sensor Korosi Pada Lingkungan Asam Menggunakan Serat Optik Berstruktur Singlemode-Multimode Coreless-Singlemode

Aisyah, Putri Yeni (2016) Rancang Bangun Sensor Korosi Pada Lingkungan Asam Menggunakan Serat Optik Berstruktur Singlemode-Multimode Coreless-Singlemode. Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[img]
Preview
Text
2212100036-Undergraduate_Thesis.pdf - Published Version

Download (3MB) | Preview

Abstract

Sensor korosi konvensional yang banyak diaplikasikan saat ini memiliki kelemahan yaitu sering menyebabkan kerusakan tambahan karena sebagian besar korosi terjadi pada tempat yang tersembunyi yang tidak dapat diperiksa secara langsung. Salah satu alternatif untuk mengatasi kelemahan sensor korosi konvensional adalah sensor korosi berbasis serat optik dengan menggunakan sistem pengukuran berbasis perubahan intensitas cahaya akibat adanya pengaruh perlakuan korosi. Jenis serat optik yang diusulkan sebagai sensor adalah serat optik berstruktur SMS agar diperoleh sensitivitas yang tinggi. Bagian serat optik multimode dilapisi dengan logam aluminium sebagai objek korosi. Perlakuan korosi yang diberikan adalah uji rendam sensor pada larutan HCl 3M. Hasil eksperimen menunjukkan bahwa pengaruh korosi terhadap daya keluaran sensor menghasilkan trend grafik naik. Dari hasil pengujian sensor secara eksperimen dengan rentang perlakuan korosi selama 9 jam terhadap daya keluaran serat optik diperoleh selisih rentang daya keluaran terbesar adalah 13.19 dBm. Hasil eksperimen juga menunjukkan sensitivitas tertinggi sensor adalah 0.094 dBm/mg pada rentang massa yang hilang dari lapisan tipis aluminium 0-140 mg dan panjang serat optik multimode adalah 10 mm ==============================================================================================Conventional corrosion sensors have been applied, but have many weakness that often cause additional damage because most corrosion occurs in a hidden place that can not be tested directly. One of the alternative to overcome the lack of conventional corrosion sensor based optical fiber using measurement system based intesity due to the influence of soaking the sensor in a corrosive solution HCl. A singlemode-multimode coreless-singlemode is used as a fiber optic sensor, because it can give a high sensitivity sensor. Part of multimode optical fiber coated with metallic aluminum as the object of corrosion. The experimental results indicate that the effect of corrosion on the power output of the sensor resulted in a trend graph rises. Experimental results is obtained that the largest of optical fiber output power is 13.19 dBm with interval soaking for 9 hours. Experimental results also show that the highest sensitivity of the sensor is 0.094 dBm/mg the span output from a thin layer of aluminium 0-140 mg and 10 mm multimode optical fiber length

Item Type: Thesis (Undergraduate)
Additional Information: RSF 681.2 Ais r-1
Uncontrolled Keywords: Serat optik SMS, serat multimode coreless, sensor korosi
Subjects: Q Science > QC Physics > QC448 Fiber optics.
Divisions: Faculty of Industrial Technology > Physics Engineering > 30201-(S1) Undergraduate Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 18 Feb 2020 06:11
Last Modified: 18 Feb 2020 06:14
URI: https://repository.its.ac.id/id/eprint/75017

Actions (login required)

View Item View Item