Pengaruh Suhu Pada Sintesis Al2o3@Tio2 Core-Shell Powder Dengan Metode Solgel Terhadap Perubahan Fasa Al2o3 Dan Tio2 Sebagai Semikonduktor Dssc (Dye Sensitized Solar Cell)

Agustin, Aprillia Dewi (2016) Pengaruh Suhu Pada Sintesis Al2o3@Tio2 Core-Shell Powder Dengan Metode Solgel Terhadap Perubahan Fasa Al2o3 Dan Tio2 Sebagai Semikonduktor Dssc (Dye Sensitized Solar Cell). Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[img]
Preview
Text
2412100023-Undergraduate_Thesis.pdf - Published Version

Download (3MB) | Preview

Abstract

Sejak pertama kali dikembangkan, usaha untuk meningkatkan efisiensi Dye Sensitized Solar Cell (DSSC) terus dilakukan. Penelitian ini melakukan modifikasi pada fotoelektroda dengan menggunakan menggunakan Al2O3@TiO2 core-shell sebagai semikonduktor. Sintesis Al2O3@TiO2 core-shell dilakukan dengan metode sol-gel menggunakan 5 variasi suhu untuk melihat pengaruhnya terhadap transformasi fasa. Pada suhu 650°C terjadi transformasi fasa anatase menjadi rutile pada TiO2 dan pada suhu 850°C untuk transformasi fasa γ- menjadi α-Al2O3. Karakterisasi FTIR menunjukkan absorpsi pada bilangan gelombang 439 nm pada semua variasi suhu kecuali pada suhu 1050°C. Karakterisasi ini mengindikasikan bahwa struktur core-shell telah terbentuk. Dari pengujian PSA, didapatkan ukuran partikel pada rentang 350 nm - 480 nm. Dari hasil pengujian di bawah sinar matahari, DSSC yang menghasilkan efisiensi terbaik adalah DSSC yang menggunakan sampel Al2O3@TiO2 core-shell dengan suhu kalsinasi 1200°C dengan efisiensi 0,000046%. Sedangkan DSSC dengan menggunakan sampel Al2O3@TiO2 core-shell dengan suhu kalsinasi 850°C menghasilkan nilai efisiensi paling kecil, yaitu sebesar 0,000017% ============================================================================================ Since it was first developed, efforts to improve the efficiency of Dye-sensitized Solar Cell (DSSC) are continously carried out. This study modified photoelectrode using Al2O3@TiO2 core-shell as semiconductor. Synthesis of Al2O3@TiO2 core-shell was carried out by sol-gel method using 5 temperature variations to observe its effect on the phase transformation. At temperature of 650°C phase transformation occured on TiO2 from anatase to rutile and at 850°C for Al2O3 phase transformation from γ-Al2O3 to α-Al2O3. FTIR characterization showed absorption at wavenumbers of 583 cm-1 and 439 cm-1 for all temperature variations except for 1050°C. This characterization indicates that the core-shell structure has been formed. The obtained particle size is in the range of 350 nm to 480 nm. I-V tests under the sunlight result in the best efficiency of DSSC for Al2O3@TiO2 core-shell calcined at 1200°C i.e. 0.000046%. While the DSSC using Al2O3@TiO2 core-shell with calcination temperature of 850°C produces the smallest efficiency i.e. 0.000017%

Item Type: Thesis (Undergraduate)
Additional Information: RSF 621.312 44 Agu p-1
Uncontrolled Keywords: Al2O3@TiO2 core-shell, metode sol-gel, efisiensi DSSC, transformasi fasa
Subjects: T Technology > TJ Mechanical engineering and machinery > TJ810.5 Solar energy
T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK2960 Dye-sensitized solar cells. Solar batteries. Solar cells
Divisions: Faculty of Industrial Technology > Physics Engineering > 30201-(S1) Undergraduate Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 19 Jun 2020 03:28
Last Modified: 19 Jun 2020 03:28
URI: https://repository.its.ac.id/id/eprint/76183

Actions (login required)

View Item View Item