Optimasi Kekuatan Tarik, Kekerasan, Dan Panjang Upset Hasil Lasan Baja Suh 3 Pada Pengelasan Gesek Menggunakan Metode Response Surface Dan Goal Programming

Muzaki, Mochamad (2018) Optimasi Kekuatan Tarik, Kekerasan, Dan Panjang Upset Hasil Lasan Baja Suh 3 Pada Pengelasan Gesek Menggunakan Metode Response Surface Dan Goal Programming. Masters thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2114201002-Master_Thesis.pdf - Accepted Version

Download (2MB) | Preview

Abstract

Metode pengelasan dalam kondisi padat sering digunakan pada proses penyambungan komponen-komponen benda kerja. Las gesek merupakan salah satu metode pengelasan kondisi padat yang menghasilkan lasan ketika dua benda kerja berputar relatif satu terhadap yang lain disertai tekanan. Pemilihan parameter untuk pengelasan gesek ini merupakan faktor yang sangat menentukan keberhasilan proses pengelasan. Dalam penelitian ini pemilihan dan optimasi parameter pengelasan dipelajari dan dianalisis dengan metode respon permukaan dan goal programming. Penelitian dilakukan menggunakan dua material sejenis, yaitu baja SUH 3 untuk mendapatkan respon kekuatan, kekerasan, dan panjang upset dari lasan. Kecepatan putaran spindel, gaya gesek, dan gaya tempa, merupakan parameter yang akan divariasikan. Hasil penelitian menunjukkan bahwa kekuatan tarik, panjang upset, dan kekerasan optimum didapatkan pada pengaturan kecepatan putaran spindel sebesar 1500, gaya gesek sebesar 5,8 kN, dan gaya tempa sebesar 10 kN. Hasil kekuatan tarik, panjang upset, dan kekersan optimum berturut-turut adalah sebesar 122,8 kgf/mm2 , 6,9 mm, dan 41,2 HRC. ======================================================================================================== Solid state welding method is often used in process of joining components of the workpiece. Friction welding is one of the solid welding method that produces a weld when two workpieces rotating relative to one another under certain pressure. Selection of the process parameter in friction welding plays an important role that determine the success of the welding process. In this research, the selection and optimation of welding parameters are studied and analyzed by the response surface method and goal programming. This work was conducted using two similar materials, SUH 3 steel, to obtain responses of tensile strength and upset length of weld. Spindle rotating speed, friction force, and forge force are parameters varied. The result show that the optimum tensile strength, upset length, and hardness is obtained in using 1500 rpm spindle rotating speed, 5,8 kN friction force, and 10 kN forge force. The optimum tensile strength, upset length, and hardness are 122,8 kgf/mm2, 6,9 mm, and 41,2 HRC, respectively.

Item Type: Thesis (Masters)
Additional Information: RTM 671.52 Muz o 3100016067681
Uncontrolled Keywords: Las gesek, Optimasi, Response surfacae, Goal programming
Subjects: T Technology > TN Mining engineering. Metallurgy > TN879.6 Welding
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21101-(S2) Master Thesis
Depositing User: Yeni Anita Gonti
Date Deposited: 15 Jul 2020 04:14
Last Modified: 15 Jul 2020 04:14
URI: https://repository.its.ac.id/id/eprint/76377

Actions (login required)

View Item View Item