Sintesis Serbuk Nano-Zirkonia Tetragonal Melalui Serbuk Zirkon Dengan Variasi Konsentrasi HCl Dan Temperatur

Valhalla, Axl Bintanis Ghafirilla (2020) Sintesis Serbuk Nano-Zirkonia Tetragonal Melalui Serbuk Zirkon Dengan Variasi Konsentrasi HCl Dan Temperatur. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
01111640000006-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only

Download (2MB) | Request a copy

Abstract

Sintesis serbuk zirkon (ZrSiO4) dari pasir zirkon alam yang berasal dari Kereng Pangi, Kalimantan Tengah, Indonesia melalui reaksi dengan HCl dan NaOH serta menggunakan variasi konsentrasi HCl 0,5; 1,0; 2,0M dan temperatur 80, 90, 100°C telah selesai dilakukan. Preparasi awal pasir zirkon alami dimulai dengan pengayakan dengan mesh 40 dengan ukuran saring 0,425 mm, kemudian separasi magnet, penggilingan menggunakan ball milling, lalu dengan pelindian HCl untuk menghasilkan serbuk zirkon. Tahap lanjutan adalah pereaksian dengan NaOH untuk mengobservasi keefektifan proses pelindian untuk menghasilkan serbuk zirkonia. Dari hasil pengujian XRF pasir zirkon alam dinyatakan bahwa dalam pasir zirkon tersebut terkandung 3 senyawa utama yaitu zirkon (ZrSiO4), silika kuarsa (SiO2), dan rutil (TiO2) dengan prosentasi Zr paling tinggi, yaitu sebesar 81,12%. Hasil uji dan analisis XRD dan XRF dari serbuk-serbuk sintesis zirkon menunjukkan bahwa kombinasi penggunaan konsentrasi HCl 0,5M dan temperatur 80°C terbukti efektif untuk menghasilkan zirkon murni. Sementara itu, produk serbuk zirkonia setelah melalui tahap zirkonia amorf dan kalsinasi 3 jam pada temperatur 700°C adalah zirkonia tetragonal dengan ukuran kristal sekitar 17 nm. ================================================================================================================== Synthesis of zircon powder (ZrSiO4) from natural zircon sand from Kereng Pangi, Central Kalimantan, Indonesia through reaction with HCl and NaOH and using variations HCl concentration 0.5, 1.0, 2.0M and temperatures 80, 90, 100°C have been completed. Initial preparation of natural zircon sand begins with sieving with mesh 40 with a filter size 0.425 mm, then magnetic separation, grinding using ball milling, then with HCl leaching to produce zircon powder. The next step is to react with NaOH to observe the effectiveness of the leach process to produce zirconia powder. From the results of the XRF natural zircon sand test it was stated that the zircon sand contained 3 main compounds namely zircon (ZrSiO4), quartz silica (SiO2), and rutile (TiO2) with the highest percentage of Zr, which was 81.12%. The results of XRD and XRF test and analysis of zircon synthesis powders showed that the combination of using 0.5M HCl concentration and 80°C temperature was proven effective to produce pure zircon. Meanwhile, the zirconia powder product after going through the amorphous zirconia and calcination stages for 3 hours at 700°C is a tetragonal zirconia with a crystal size of around 17 nm.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: pelindian HCl, zirkon, alkali fusion, zirkonia, HCl leaching, zircon, alkaline fussion, zirconia
Subjects: Q Science
Q Science > QC Physics
Q Science > QC Physics > QC585.75.S55 Silica
Divisions: Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User: AXL BINTANIS GHAFIRILLA VALHALLA
Date Deposited: 06 Aug 2020 06:38
Last Modified: 06 Aug 2020 06:38
URI: https://repository.its.ac.id/id/eprint/76708

Actions (login required)

View Item View Item