Perbaikan Sifat Mekanik Dan Sifat Termal Pada Polimer Daur Ulang Menggunakan Komposit Clay

Noviaji, Anggit Irawan (2016) Perbaikan Sifat Mekanik Dan Sifat Termal Pada Polimer Daur Ulang Menggunakan Komposit Clay. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2414105030-Undergraduate_Thesis.pdf]
Preview
Text
2414105030-Undergraduate_Thesis.pdf - Accepted Version

Download (1MB) | Preview

Abstract

Telah dilakukan penelitian pada bahan komposit berbasis
polipropilena daur ulang dengan filler clay dengan dua macam ukuran
partikel clay yaitu 1 μm dan 74 μm. Komposisi clay mempunyai variasi
yaitu 3 %, 5%, dan 8 % berat. Sifat mekanik dan sifat termal pada
polimer daur ulang umumnya mengalami penurunan, sehingga
diharapkan dengan menjadikan polimer daur ulang tersebut menjadi
komposit diharapkan akan meningkatkan sifat-sifat tersebut. Pengujian
sifat mekanik dan termal dilakukan dengan tes DMA (Dynamic
Mechanical Analysis). Penambahan clay memperkecil massa jenisnya,
sehingga material komposit menjadi lebih ringan. Untuk penambahan
konsentrasi yang diberikan, maka massa jenis dari komposit polimer
akan meningkat dengan kecenderungan untuk ukuran 1 μm memiliki
massa jenis yang lebih besar dibandingkan dengan ukuran partikel 74
μm dengan perbandingan pada variasi konsentrasi clay yang diberikan
adalah sama. Dengan menambahkan clay ke dalam polipropilen akan
meningkatkan sifat mekanik dan sifat termalnya. Sifat termal terbaik
didapatkan pada penambahan konsentrasi clay 8% dengan ukuran
partikel 74 μm dengan nilai Tg adalah 48oC. Sifat mekanik terbaik
diperoleh pada penambahan konsentrasi clay 5% pada ukuran partikel 1
μm
==================================================================================================================
It has been conducted a research on composite materials based on
recycled polypropylene with clay filler having two kinds of clay particle
size i.e. 1 μm and 74 μm. The composition of clay was varied of 3%, 5%
and 8% by weight. Mechanical properties and thermal properties of the
recycled polymers are generally decreased, by recycling polymer into
composite. It is expected improve making these properties will be
improved. Mechanical properties and thermal tests were conducted by
DMA (Dynamic Mechanical Analysis). The addition of clay reduces
its density, thus composite materials become lighter. For all clay
concentrations studied the density of composite having 1 μm clay always
somewhat higher than those 74 μm size. By adding clay into
polypropylene the mechanical properties and thermal properties will
improved. Best thermal properties obtained for the addition of clay 8%
with particle size of 74 μm with a Tg value is 48oC. Best mechanical
properties obtained for the addition of clay 5% with particle size of 1
μm

Item Type: Thesis (Undergraduate)
Additional Information: RSF 620.118 Nov p
Uncontrolled Keywords: clay; polimer; komposit; DMA
Subjects: Q Science > QC Physics > QC173.4.C63 Composite materials
Divisions: Faculty of Industrial Technology > Physics Engineering > 30201-(S1) Undergraduate Thesis
Depositing User: ansi aflacha
Date Deposited: 30 Jul 2020 02:56
Last Modified: 30 Jul 2020 02:56
URI: http://repository.its.ac.id/id/eprint/76716

Actions (login required)

View Item View Item