DETEKSI KELEMBABAN RELATIF MENGGUNAKAN SERAT OPTIK PLASTIK MULTIMODE STEP-INDEX BERBASIS POLYVINYL ALCOHOL

Hairunisa, Hairunisa (2020) DETEKSI KELEMBABAN RELATIF MENGGUNAKAN SERAT OPTIK PLASTIK MULTIMODE STEP-INDEX BERBASIS POLYVINYL ALCOHOL. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
01111640000091-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only

Download (2MB) | Request a copy

Abstract

Pada penelitian ini dilakukan pendeteksian kelembaban relatif dengan menggunakan serat optik plastik jenis multimode step-index dengan variasi panjang pengupasan 2 cm dan 4 cm. Serat optik tersebut dilapisi dengan Polyvinyl Alcohol (PVA). Sumber cahaya dan detektor yang digunakan adalah BF5R-D1-N. Pendeteksian kelembaban relatif dilakukan pada rentang 62% RH – 92% RH. Lapisan PVA dapat mendeteksi perubahan kelembaban dengan mengalami penggembungan (swell) saat diberi kelembaban. Intensitas cahaya akan mengalami kenaikan seiring dengan meningkatnya kelembaban. Panjang kupasan berpengaruh pada intensitas, linieritas, dan rentang deteksi. Serat optik dengan panjang kupasan yang lebih besar akan menghasilkan intensitas yang lebih kecil. Linieritas Sampel 1, 2, dan 3 yang diperoleh pada penelitian ini secara berturut-turut 0,97562, 0,98451, dan 0,98857. Pada penelitian ini Sampel 2 merupakan sampel yang paling optimum karena dapat merespon kenaikan kelembaban dengan baik pada rentang 65% RH – 92% RH. ========================================================= This research presents detection of relative humidity using multimode step-index plastic optical fiber, with stripping length variations 2 cm and 4 cm. The fiber optic are coated with Polyvinyl Alcohol (PVA). BF5R-D1-N is used as light source and detector. The humidity detection of this research is in the range of 62% RH – 92% RH. The PVA coating is able to detect the changes of humidity because it will swell after absorbing water vapor. The intensity will rise as the rising of humidity. The stripping length of fiber optic affects the intensity, linearity, and the range of detection. The fiber optic with longer stripping length has smaller intensity. The linearity of Sample 1, 2, and 3, consecutively; are 0,97562, 0,98451, and 0,98857. In this research Sample 2 with stripping length 2 cm is the optimum sample because it has a good response to the raise of humidity in the range of 65% RH – 92% RH.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Cladding, Kelembaban, Polyvinyl Alcohol, Serat Optik Plastik, Cladding, Humidity, Plastic Optical Fiber, Polyvinyl Alcohol
Subjects: Q Science > QC Physics > QC448 Fiber optics.
Divisions: Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User: Hairunisa Hairunisa
Date Deposited: 03 Aug 2020 07:33
Last Modified: 03 Aug 2020 07:33
URI: https://repository.its.ac.id/id/eprint/76802

Actions (login required)

View Item View Item