Abstract

Silika nanotube merupakan nanomaterial silika yang memiliki luas permukaan yang tinggi dengan ukuran pori yang besar daripada silika pada umumnya serta memiliki struktur seperti tabung. Sintesis silika nanotube umumnya menggunakan bahan konvensional seperti teraetil orthosilikat(TEOS). Namun, penggunaan tersebut dapat diganti dengan bahan yang lebih ekonomis dan ramah lingkungan seperti sekam padi yang mengandung sekitar 89-97% berat silika. Sintesis silika nanotube umumnya membutuhkan template sebagai pendukung untuk mengubah strukturnya menjadi bentuk tabung. Namun, diperlukan metode sintesis tertentu untuk menghasilkan silika nanotube yang baik. Tujuan dari review paper ini yaitu untuk menganalisis pengaruh metode sintesis terhadap pembentukan silika nanotube baik itu metode hidrotermal, sol-gel, dan electrospinning, serta menganalisis perbandingan metode sintesis untuk menghasilkan silika nanotube. Dari hasil paper review tersebut, didapat bahwa metode hidrotermal yang paling baik dilihat dari struktur silika nanotube yang dihasilkan dengan rata-rata ukuran pori dan luas permukaan spesifik sebesar 2-10 nm dan 900 1500 m2/g serta serbuk yang dihasilkan lebih reaktif.
=========================================================
Silica nanotubes are silica nanomaterials that have a high surface area with a bigger pore size than silica in general and have a tube-like structure. Synthesis of silica nanotubes generally uses conventional materials such as teraethyl orthosilicate (TEOS). However, these uses can be replaced with more economical and environmentally friendly materials such as rice husks which contain around 89-97% by weight of silica. Synthesis of silica nanotubes generally requires a template as a support to convert its structure into a tubular shape. However, certain synthesis methods are needed to produce good silica nanotubes. The purpose of this paper review is to analyze the effect of the synthesis method on the formation of silica nanotubes in the form of hydrothermal, sol-gel and electrospinning methods, and analyze the comparison of synthesis methods to produce silica nanotubes. From the results of the review paper, it was found that the hydrothermal method is best seen from the structure of silica nanotubes produced with an average pore size and specific surface area of 2-10 nm and 900-1500 m2/g and and the powder produced is more reactive.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: silica nanotube, rice husk, hydrothermal, electrospinning, sol-gel
Subjects: Q Science
Q Science > QC Physics > QC585.75.S55 Silica
T Technology > T Technology (General)
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: M. Dayyan Naharevy
Date Deposited: 11 Aug 2020 03:06
Last Modified: 19 May 2023 14:23
URI: http://repository.its.ac.id/id/eprint/77384

Actions (login required)

View Item View Item