Review: Pengaruh Penggunaan Template Terhadap Pembentukan Silika Nanotubes Berbahan Dasar Sekam Padi

Ferawati, Triska (2020) Review: Pengaruh Penggunaan Template Terhadap Pembentukan Silika Nanotubes Berbahan Dasar Sekam Padi. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
02511640000041-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only

Download (2MB) | Request a copy

Abstract

Silika nanotubes merupakan salah satu jenis nanopartikel dari senyawa silika, dengan struktur berbentuk tabung. Di mana, sifat yang dimiliki tidak sama dengan silika pada umumnya. Umumnya, silika nanotubes dapat disintesis menggunakan beberapa metode, dengan tetap mengacu pada penggunaan template sebagai pengarah struktur. Di mana, bahan dasar utama yang digunakan berupa tetraethyl orthosilicate. Namun karena beberapa kekurangan yang dimilikinya, maka penggunaan bahan tersebut dapat digantikan dengan sekam padi, yang memiliki kandungan silika sebesar 80-90%. Adapun tujuan penulisan paper review ini yaitu untuk menganalisis pengaruh penggunaan template terhadap struktur silika nanotubes, baik berupa soft template maupun hard template, serta menganalisis perbandingan template yang digunakan. Dari hasil paper review ini, diperoleh bahwa penggunaan template sangat berpengaruh terhadap pembentukan silika nanotubes. Di mana, penggunaan material soft template dinilai lebih baik dan efisien. Hal ini dikarenakan ukuran pori yang dihasilkan cukup seragam yaitu 2-11 nm, dengan rata-rata luas permukaan spesifik dan total volume pori yang cukup tinggi yaitu sebesar 350-1500 m2/g dan 0,04-2,5 cm3/g, serta proses pelepasan templatenya yang tidak begitu rumit. ============================================================ Silica nanotubes are one of the nanoparticle types made from silica compounds with a tubular structure. The properties of silica nanotubes are not the same as silica in general. Generally, silica nanotubes can be synthesized using several methods, while still referring to the use of templates as structural guides. The main ingredient used is tetraethyl orthosilicate. However, due to some disadvantages, the use of this material can be replaced with rice husk, which has a silica content of 80-90%. The purpose of writing this paper review is to analyze the effect of the use of templates on the structure of silica nanotubes, both in the form of soft templates and hard templates, also to analyze the comparison of the templates used. From the results of this paper review, it was found that the use of templates is very influential in the formation of silica nanotubes. Where the use of soft template material is considered better and more efficient. This is because the resulting pore size is fairly uniform started from 2-11 nm, with an average specific surface area and a high total pore volume is 350-1500 m2/g and 0.04-2.5 cm3/g, and the release process of the template is not so complicated.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Hard template, Rice husk, Silica nanotubes, Soft template, Hard template, Sekam padi, Silika nanotubes, Soft template.
Subjects: Q Science > QD Chemistry
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Triska Ferawati
Date Deposited: 12 Aug 2020 04:50
Last Modified: 12 Aug 2020 04:50
URI: https://repository.its.ac.id/id/eprint/77636

Actions (login required)

View Item View Item