REVIEW PENGARUH ELEMEN PADUAN TERHADAP PERTUMBUHAN PRESIPITAT PADA PADUAN Al-Si-Mg-Cu SELAMA PROSES AGE HARDENING

Nuhung, Na'il AKbar (2020) REVIEW PENGARUH ELEMEN PADUAN TERHADAP PERTUMBUHAN PRESIPITAT PADA PADUAN Al-Si-Mg-Cu SELAMA PROSES AGE HARDENING. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
02511640000097-Undergraduate_Thesis .pdf - Accepted Version
Restricted to Repository staff only

Download (4MB)

Abstract

Paduan Al-Si-Mg-Cu merupakan salah satu paduan yang dapat ditingkatkan kekuatan dan kekerasannya dengan cara diberi perlakuan panas yang disebut age hardening. Meningkatnya sifat mekanik paduan aluminium dengan proses age hardening dapat terjadi karena adanya medan regangan pada struktur mikro yang disebabkan oleh ikatan koheren dari tumbuhnya presipitat. Efektifitas age hardening sangat bergantung pada jenis, jumlah, ukuran dan persebaran dari presipitat dengan ukuran nano. Efektifitas proses presipitasi dan jenis presipitat yang terbentuk sangat bergantung pada kadar paduan yang terlarut pada matriks Al. Paper review ini akan membahas pertumbuhan masing-masing presipitat β"-Mg2Si, Q’-Al3.8Mg8.6Si7Cu1 dan θ'-Al2Cu pada paduan Al-Si-Mg-Cu yang dipengaruhi oleh unsur paduan pada proses age hardening. Efektifitas age hardening semakin tinggi dengan pertumbuhan cepat presipitat β", yang kemudian digantikan presipitat halus θ' di kondisi peak aging pada kadar Cu tinggi. Ditemukannya presipitat θ' pada kondisi peak aging juga menunjukan meningkatnya sifat mekanik paduan Al-Si-Mg-Cu. Secara komposisi pembentukan presipitat θ' hanya bergantung pada unsur paduan Cu, dimana pada kadar Cu 4-4.5% ditemukan presipitat halus θ' dalam jumlah yang paling banyak. Namun, efektifitas petumbuhannya juga bergantung pada presipitat Q’ yang dapat terbentuk dengan penambahan kadar Mg dan Si. Selain itu rapid hardening yang diakibatkan pertumbuhan presipitat β" pada tahap awal proses age hardening semakin meningkatkan sifat mekanik paduan Al-Si-Mg-Cu. Hal ini menunjukan ketiga presipitat pada paduan Al-Si-Mg-Cu memiliki peranan penting pada meningkatnya sifat mekanik paduan melalui proses age hardening. ========================================================= Age hardening has been recognized as methods for strengthening Al-Si-Mg-Cu alloys. Age hardening's process which involves strengthening the alloys by coherent precipitates which capable of withstand dislocation. Effect of age hardening depending on the kind, amount, size, and uniform of the precipitate, which involves alloy elements dissolve in aluminium. This paper will review the growth of precipitates (β"-Mg2Si, Q'-Al3.8Mg8.6Si7Cu1 dan θ'-Al2Cu) influenced by containing alloy in Al-Si-Mg-Cu alloys during age hardening. Al-Si-Mg-Cu responds to age hardening depending on rapid hardening influenced by high nucleation rate precipitate β" and formation Q', which would accelerate growth precipitate θ' and result fine precipitate θ'. In composition, precipitate θ' influenced only by composition Cu, when alloy with Cu 4-4.5wt% observed fine precipitate θ' at the most. however, nucleation and growth θ' depending on formation Q', which influenced by composition Mg and Si. Furthermore, a high nucleation rate of β" resulted in rapid hardening alloy on the initial stage of artificial aging. In conclusion, all three of the precipitate played a crucial role in the improved mechanical properties of aluminium alloy by the process of age hardening.

Item Type: Thesis (Undergraduate)
Subjects: T Technology > TN Mining engineering. Metallurgy > TN775 Aluminum alloys--Metallurgy.
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Na'il Akbar Nuhung
Date Deposited: 12 Aug 2020 04:23
Last Modified: 12 Aug 2020 04:23