Review Pengaruh Anodizing dengan Variasi Beda Potensial dan Konsentrasi Elektrolit terhadap Morfologi dan Ketebalan Lapisan Pasif ZnO untuk Aplikasi Hot-Dip Galvanized Steel

Barran, Muhammad Ghilman (2020) Review Pengaruh Anodizing dengan Variasi Beda Potensial dan Konsentrasi Elektrolit terhadap Morfologi dan Ketebalan Lapisan Pasif ZnO untuk Aplikasi Hot-Dip Galvanized Steel. Other thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 02511640000144-Undergraduate_Thesis.pdf]
Preview
Text
02511640000144-Undergraduate_Thesis.pdf

Download (2MB) | Preview

Abstract

Korosi merupakan masalah yang perlu dihadapi khususnya bagi peralatan yang menggunakan logam sebagai material utamanya, sehingga perlu cara untuk memperlambat laju korosi tersebut. Galvanized steel merupakan pelapisan baja menggunakan zinc sebagai proteksi katodik. Namun pada lingkungan laut yang korosif membuat korosi lebih cepat terjadi, sehingga perlu metode untuk meningkatkan ketahanan korosi pada baja galvanis tersebut. Anodizing merupakan metode untuk meningkatkan ketahanan korosi dengan membentuk lapisan oksida pada permukaan substrat. Review ini dilakukan dengan tujuan untuk menganalisis pengaruh beda potensial dan konsentrasi larutan elektrolit pada anodizing terhadap morfologi dan ketebalan lapisan anodik. Proses anodizing dilakukan dengan variasi dari beda potensial dan konsentrasi larutan elektrolit. Karakterisasi meliputi XRD, SEM, dan untuk mengetahui laju korosi yang dihasilkan digunakan uji Tafel dan Weight Loss. Dari hasil paper review didapatkan struktur dari material adalah ZnO, semakin tinggi beda potensial maka semakin tebal lapisan pasif yang dihasilkan, jumlah zinc yang terdisolusi lebih banyak dan terjadi porositas dan fenomena retak, sementara pada peningkatan konsentrasi elektrolit, semakin tebal lapisan pasif yang dihasilkan, jumlah zinc yang terdisolusi lebih banyak, dan terdapat lebih banyak lubang pada permukaan, dan untuk laju korosi yang dihasilkan pada pada penggunaan anodizing akan memperlambat laju korosi.
==================================================================================================================Corrosion is a major problem for tools that use metal as the main material, a method is needed to minimize the corrosion rate of the metal. Galvanized steel is a steel coating using zinc as a cathodic protection. However, in a corrosive marine environment that makes corrosion more rapid, a method is needed to increase the corrosion resistance of the galvanized steel. Anodizing is a method for increasing corrosion resistance by forming an oxide layer on the surface of the substrate. This review was conducted with the aim of analyzing the effect of voltage and electrolyte concentration solutions of anodizing on the morphology and thickness of anodic layers. The anodizing process is carried out with variations of the voltage and concentration of the electrolyte solution. From the paper review results obtained the structure of the material is ZnO, the higher the potential difference, the thicker passive layer produced, the more amount of zinc dissolved and porosity and cracking phenomenon, while the increase in electrolyte concentration, the thicker the passive layer produced, the amount more zinc is dissolved, and more holes on the surface, and the rate of corrosion that results in the use of anodizing will decrease corrosion rate.

Item Type: Thesis (Other)
Uncontrolled Keywords: Anodizing, Zinc, Konsentrasi Elektrolit, Morfologi, Beda Potensial Anodizing, Zinc, Electrolyte Concentration Morphology, Voltage
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA491 Metal coating.
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Muhammad Ghilman Barran
Date Deposited: 12 Aug 2020 04:06
Last Modified: 25 May 2023 13:03
URI: http://repository.its.ac.id/id/eprint/77692