Pengaruh Doping Zn pada CuO Sebagai Fotokatoda Dye-Sensitized Solar Cell (DSSC) Tipe P

Arandani, Chiara (2020) Pengaruh Doping Zn pada CuO Sebagai Fotokatoda Dye-Sensitized Solar Cell (DSSC) Tipe P. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
02311640000150-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only

Download (3MB) | Request a copy

Abstract

Energi sangat dibutuhkan untuk menopang berbagai aspek kehidupan manusia. Salah satu sumber energi yang dapat dimanfaatkan sebagai energi baru dan terbarukan adalah matahari. Menggunakan sel surya, sinar matahari dapat dikonversikan menjadi energi listrik berkualitas tinggi secara langsung. Salah satu jenis sel surya yang saat ini sedang banyak dikembangkan adalah Dye-Sensitized Solar Cell (DSSC), yaitu thin film solar cell berbasis semikonduktor yang terbentuk diantara fotoanoda atau fotokatoda dan elektrolit, serta dengan pemanfaatan pewarna di dalamnya. Akhir-akhir ini, DSSC dengan semikonduktor tipe p, yaitu CuO, mulai dijadikan fokusan penelitian. Pada penelitian ini, CuO didoping dengan Zn, dimana doping tersebut dilakukan untuk merubah sifat CuO. Konsentrasi doping Zn divariasikan, yakni 0, 8, 10, 12, dan 14 mol%. Zn akan memengaruhi diameter kristal menjadi lebih besar, lebar spektrum absorbansi ke arah cahaya tampak, memperkecil celah pita energi CuO, dan meningkatkan performansi DSSC. Hasil akhir penelitian ini didapatkan bahwa Zn meningkatkan diameter kristal dari 38,415 nm menjadi 56,892 nm, mempersempit celah pita energi CuO dari 3,02 eV menjadi 2,9 eV dan meningkatkan efisiensi DSSC dari 0,000163% menjadi 0,000748%. ========================================================= Energy is needed to sustain various aspect of human life. One of the energy sources that can be used as a new and renewable energy is the sun. Solar cells can be used to convert sunlight directly to high quality electrical energy. One of the solar cells that is currently being developed is Dye-Sensitized Solar Cell (DSSC), which is a semiconductor based thin film solar cell that is formed between a photoanode or photocatode and an electrolyte, also with the use of a dye. Lately, DSSC with p type semiconductor, CuO, are starting to become the focus of researches. In this research, CuO is doped with Zn to change the characteristics of CuO. Zn will affect in increase in diameter of the crystal, width of the absorbance spectrum, reduction the CuO’s energy band gap, and improvement of DSSC’s performance. The results of this research found that Zn increased the crystal’s diameter from 38.415 nm to 56.892 nm, narrowed the CuO’s energy band gap from 3.02 eV to 2.9 eV and increased the DSSC’s efficiency from 0.000163% to 0.000748%.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: CuO, doping Zn, DSSC, CuO, DSSC, Zn doped
Subjects: T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK2960 Dye-sensitized solar cells. Solar batteries. Solar cells
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Physics Engineering > 30201-(S1) Undergraduate Thesis
Depositing User: Chiara Arandani
Date Deposited: 13 Aug 2020 12:36
Last Modified: 13 Aug 2020 12:36
URI: https://repository.its.ac.id/id/eprint/78052

Actions (login required)

View Item View Item