FABRIKASI DYE SENSITIZED SOLAR CELL (DSSC) TIPE P DENGAN FOTOKATODA Cu2O NANOCUBE

Anggraini, Rachma (2020) FABRIKASI DYE SENSITIZED SOLAR CELL (DSSC) TIPE P DENGAN FOTOKATODA Cu2O NANOCUBE. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
02311640000102-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only

Download (2MB) | Request a copy

Abstract

Cuprous oxide (Cu2O) merupakan semikonduktor tipe p dengan band gap sekitar 1,8 eV-2,2 eV dimana sesuai untuk fotokatoda DSSC. Selain itu Cu2O tidak beracun, banyak tersedia di alam, memiliki band gap yang dapat diubah-ubah. Pada penelitian ini dilakukan fabrikasi DSSC tipe p dengan semikonduktor Cu2O sebagai fotokatoda. Ukuran Cu2O divariasikan dengan mengubah konsentrasi NaOH pada sintesis. Cu2O disintesis dengan prekursor Cu(CH3COO)2·H2O dan agen pereduksi asam askorbat dan NaOH. Hasil XRD dari Cu2O menunjukkan bahwa struktur kristal Cu2O adalah kubik. Variasi konsentrasi NaOH yang digunakan saat sintesis berpengaruh pada ukuran partikel yang terbentuk. Peningkatan konsentrasi NaOH menyebabkan meningkatnya ukuran partikel Cu2O. Semakin kecil ukuran partikel band gap Cu2O semakin bertambah besar. Band gap Cu2O didapatkan sebesar 2,44 eV, 2,35 eV, 2,12 eV, 2,1 eV, dan 2,09 eV untuk variasi konsentrasi NaOH sebesar 0.075 M, 0,113 M, 0,188 M, 0,263 M, dan 0,3 M secara berturut-turut. Performansi DSSC didapatkan yang paling baik pada konsentrasi NaOH sebesar 0,3 M ditunjukan dengan efisiensi sebesar 0,00119 %. ========================================================================= Cuprous oxide (Cu2O) is a p-type semiconductor with a 1.8 eV-2.2 eV bandgap which has potential applications on DSSC photocathode. Cu2O is non-toxic material, earth-abundant, and has a tunable bandgap. In this research, Cu2O as photocathode in p-type DSSC was synthesized in various sizes. The size of the Cu2O was tailored by adjusting the concentration of the NaOH solution. Cu2O was synthesized by the reduction of Cu(CH3COO)2·H2O precursor using ascorbate acid and NaOH. XRD spectra exhibited that the Cu2O structure is cubic. Increased NaOH concentration augments the Cu2O particle size. Cu2O optical band gap increases as particle size decreases. Obtained Cu2O optical band gaps were 2.44 eV, 2.35 eV, 2.12 eV, 2.1 eV, and 2.09 eV for 0.075 M, 0.113 M, 0.188 M, 0.263 M, and 0.3 M NaOH concentrations, respectively. The highest DSSC efficiency obtained was 0.0019% for the sample reduced at 0.3 M solution of NaOH.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: fotokatoda, Cu2O nanocube, efisiensi DSSC, photocatode, Cu2O nanocube, DSSC efficiency
Subjects: T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK2960 Dye-sensitized solar cells. Solar batteries. Solar cells
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Physics Engineering > 30201-(S1) Undergraduate Thesis
Depositing User: Rachma Putri Anggraini
Date Deposited: 14 Aug 2020 04:12
Last Modified: 14 Aug 2020 04:12
URI: https://repository.its.ac.id/id/eprint/78080

Actions (login required)

View Item View Item