PROSES PEMISAHAN BITUMEN DARI BATUAN ASBUTON DENGAN PROSES MILLING DAN PENAMBAHAN SURFAKTAN

Rinanda, Zalza Lola (2020) PROSES PEMISAHAN BITUMEN DARI BATUAN ASBUTON DENGAN PROSES MILLING DAN PENAMBAHAN SURFAKTAN. Masters thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
02211850010010-Master_thesis.pdf
Restricted to Repository staff only

Download (599kB) | Request a copy

Abstract

Indonesia merupakan Negara yang kaya akan sumberdaya alamnya. Salah satunya yang kurang terkembangkan adalah aspal Buton (Asbuton). Asbuton sendiri dimanfaatkan sebagai bahan alternatif pengganti aspal minyak, yang sudah semakin sedikit. Namun kendalanya aspal dalam asbuton dilindungi oleh mineral yang perlu dipisahkan menggunakan proses tertentu. Penelitian pemisahan bitumen dari asbuton menggunakan hot water process sebelumnya telah dilakukan, tetapi bitumen yang terlepas dari mineralnya kurang maksimal. Maka dilakukannya modifikasi proses yang mempengaruhi proses pelepasan aspal tersebut, untuk meningkatkan recovery. Salah satunya dengan penambahan surfaktan Sodium Dodecyl Benzene Sulfnate (SDBS) dan wetting agent berupa Natrium Hidroksida (NaOH). Fokus dari penelitian ini adalah mempelajari pengaruh penambahan surfaktan dan wetting agent terhadap recovery bitumen. Proses pemisahan bitumen dari asbuton dalam metode ini dilakukan melalui proses milling. Proses dilakukan dengan cara mencampur asbuton dengan solar yang jumlahnya perbandingan antara bitumen dengan solarnya sebesar(rbs) 1:2 dan 1:3 Selanjutnya dilakukan proses milling dengan mencampur campuran solar- asbuton dengan larutan surfaktan dan wetting agent sebesar 20% terhadap massa campuran total. Konsentrasi campuran larutan surfaktan SDBS dan NaOH sebesar 25%, 30% dan 35%. Larutan hasil proses milling kemudian dipisahkan secara 3 fase. Lapisan teratasnya kemudian ditimbang dan dihitung massa jenisnya. Berdasarkan massa jenis larutan yang diperoleh, maka konsentrasi bitumen dapat ditentukan menggunakan kurva kalibrasi. Hasil dari penelitian ini bahwa peningkatan rasio wetting agent dan peningkatan cycle menyebabkan penurunan recovery. Recovery tertinggi sebesar 97% di peroleh pada kondisi rasio wetting agent 15 % dengan perbandingan bitumen-solar 1:3 dan pengulangan 5 cycle. ==================================================================================== Indonesia is a country that has a lot of natural resources. One of them is Buton’s asphalt rocks or asbuton. In spite of its many resources, asbuton is not efficiently used. Asbuton as a natural asphalt contains minerals that had to be separated to get its bitumen. Bitumen is the preferred geologic term for the sticky, highly viscous semi-solid hydrocarbon presents in most natural petroleum. It mostly contains pitch, resin, and asphalt. Bitumen is a natural hydrocarbon and has mostly replaced tar as the binding agent in asphalt-based roads. Bitumen separation research using hot water process has already been conducted before, but the recovery hasn’t reach an optimum value. Hence the process is modified, by adding Sodium Dodecyl Benzene Sulfonate (SDBS) as surfactant and Natrium Hidroxide (NaOH) as wetting agent. The aim of this research is to study on the effect of wetting agent and surfactant addition to recovery by using milling process. This process include mixing asbuton and diesel fuel, with ratio(rbs) 1:2 ; 1:3. Then adding a mixture of NaOH and SDBS 20% of total mass. Concentration of this mixture used in this research is 25%, 30%, and 35%. The result of this process then separated in 3 phases. The top layer which contains diesel fuel and bitumen then weighed and the density can be calculated. Based on these data, bitumen’s recovery can be known using calibration curve. From this research can be concluded that , it is found that the increase in the ratio of wetting agent and increase in cycle causes a decrease in recovery. The highest recovery is 97% obtained in the condition of 15% wetting agent ratio with 1: 3 bitumen-solar ratio and 5 cycle repetition.

Item Type: Thesis (Masters)
Uncontrolled Keywords: Asbuton, Bitumen, Proses Milling, Sodium Dodecyl Benzene Sulfonate, asbuton, bitumen, Milling Process, Sodium Dodecyl Benzene Sulfonate
Subjects: Q Science > QD Chemistry > QD63 Extraction
Q Science > QD Chemistry > QD63.S4 Separation (Technology)
Divisions: Faculty of Industrial Technology > Chemical Engineering > 24101-(S2) Master Thesis
Depositing User: Zalza Lola Rinanda
Date Deposited: 26 Aug 2020 03:40
Last Modified: 26 Aug 2020 03:40
URI: https://repository.its.ac.id/id/eprint/80817

Actions (login required)

View Item View Item