Pengukuran dan Analisa Nilai Koefisien Gesek Pada Material Resin Epoxy Reinforced Grafit

Kurniawan, Wahyu (2020) Pengukuran dan Analisa Nilai Koefisien Gesek Pada Material Resin Epoxy Reinforced Grafit. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
02111645000026_Undergraduted_Thesis.pdf - Accepted Version
Restricted to Repository staff only

Download (1MB) | Request a copy

Abstract

Pada suatu material yang mengalami kontak dengan material lain akan menimbulkan gaya gesek, gaya gesek sendiri dikatagorikan menjadi dua yaitu gaya gesek statis dan kinetis. Perubahan gaya gesek dari statis ke kinetis disebut stick-slip friction. Pada area terjadinya stick slip friction, nilai dari gaya gesek yang terjadi mempunyai nilai yang paling besar, sehingga fenomena stick-slip friction ini cukup berpengaruh terhadap umur pakai dari suatu material. Pada tugas akhir ini akan dilakukan pengukuran koefisien gesek terhadap material resin epoxy yang diberikan penguat berupa grafit untuk mengetahui koefisien gesek. Penelitian ini bertujuan untuk mengetahui bagaimana pengaruh dari penambahan grafit dan variasi pembebanan terhadap nilai koefisien gesek dari material resin epoxy yang nantinya dapat digunakan sebagai acuan alternatif material pengganti untuk keperluan-keperluan tertentu. Pengujian dilakukan dengan menggunakan force sensor, motion sensor dan perangkat lunak pasco caopstone. Material yang digunakan berupa resin epoxy reinforced grafit dengan fraksi volume sebesar,7% serta material resin epoxy tanpa penambahan reinforced grafit. Lintasan atau alas yang digunakan berupa plat alumunium. Pengujian dilakukan dengan menarik force sensor yang terhubung dengan baki uji dengan tangan. Variasi beban yang digunakan sebesar 250gr,500gr,750gr,dan 1000gr. Berdasarkan penelitian yang telah dilakukan, menujukkan bahwa nilai koefisien gesek tidak meningkat secara berbanding lurus dengan berat beban yang di berikan, nilai µs untuk resin dengan penambahan grafit untuk pembebanan 250gr, 500gr, 750gr, dan 1000gr adalah 0.454, 0.501, 0.385, dan 0.409. Penambahan bubuk grafit pada material resin epoxy dapat memperkecil jarak antara nilai µs dan µk pad grafik bila di bandingkan dengan grafik resin tanpa grafit, apabila membandingkan nilai µs untuk resin dangan dan tanpa penambahan grafit terlhat nilai µs resin dengan grafit sedikit lebih rendah. Untuk nilai µk hal tersebut berbeda dengan nilai µs pada resin dengan grafit pada saat pengujian, kurva yang relatif berhimpit dan beberapa d titik pembebana menunjukan µk lebih tinggi di banding µs. ========================================================= Material that is in contact with another material it will cause friction force, the friction force itself is categorized into two, static and kinetic friction. The change in friction from static to kinetic is called stick-slip friction. In the area where the stick-slip friction occurs, the value of the friction force that occurs has the greatest value, so that the stick-slip friction phenomenon affects the service life of a material. In this final project, the measurement of the coefficient of friction on the epoxy resin material which is given reinforcement in the form of graphite will be carried out to determine the coefficient of friction. This study aims to determine the effect of adding graphite and variations in loading on the friction coefficient value of the epoxy resin material which can later be used as an alternative reference for substitute materials for certain purposes. The test was carried out using a force sensor, motion sensor and Pasco Caopstone software. The materials used were epoxy resin reinforced graphite with a volume fraction of 7% and epoxy resin material without the addition of reinforced graphite. The track or base used is an aluminum plate. The test is done by pulling the force sensor connected to the test tray by hand. Variations in the load used are 250gr, 500gr, 750gr, and 1000gr. Based on the research, it shows that the friction coefficient value does not increase directly proportional to the weight of the given load, the µs value for the resin with the addition of graphite for the load of 250gr, 500gr, 750gr, and 1000gr is 0.454, 0.501, 0.385, and 0.409. The addition of graphite powder to the epoxy resin material can reduce the distance between the µs and µk values on the graph when compared with the graphite resin without graphite, when comparing the µs value for resin with and without the addition of graphite, it can be seen that the µs value of resin with graphite is slightly lower. For the µk value it is different from the µs value of the resin with graphite at the time of testing, the curve is relatively coincided and the several d loading points show the µk is higher than the µs.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Resin epoxy,Gaya Gesek,Penambahan Grafit,Statis,Kinetis,Epoxy Resin,Friction Force, Graphite,Static,Kinetic
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User: Wahyu Kurniawan
Date Deposited: 02 Sep 2020 02:57
Last Modified: 02 Sep 2020 02:57
URI: https://repository.its.ac.id/id/eprint/81711

Actions (login required)

View Item View Item