Sintesis Polivin Asetat Pelarut Sintesis Polivinber Metanol:Air 1:3 Dengan Variasi Jenis Surfaktan

Amalya, Ria (2014) Sintesis Polivin Asetat Pelarut Sintesis Polivinber Metanol:Air 1:3 Dengan Variasi Jenis Surfaktan. Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[img]
Preview
Text
1410100056-Undergraduate_Thesis.pdf - Published Version

Download (1MB) | Preview

Abstract

Sintesis PVAc berbasis metanol telah berhasil dilakukan dengan menggunakan monomer vinyl asetat dan variasi beberapa surfaktan yaitu Disponil FES 27 IS; Disponil A 1080; Disponil AES 72; Disponil AFX 3070. Penelitian ini dilakukan dengan proses polimerisasi emulsi dengan menggunakan reaktor kaca yang didesain khusus untuk reaksi polimerisasi. Hasil sintesis kemudian dianalisis dengan Fourier Transform Infrared (FTIR) yang menunjukkan bahwa tidak ada pengaruh surfaktan pada pembentukan gugus fungsi dalam hasil sintesis, dibuktikan dengan spektrum yang dihasilkan semua memiliki puncak yang sama. Berdasarkan pengujian viskositas lateks, hasil terbaik ditunjukkan dari penggunaan surfaktan AFX 3070. Dari analisis menggunakan Thermomechanical Analysis (TMA) menunjukkan bahwa hasil terbaik didapatkan dari penggunaan surfaktan Disponil A 1080 dengan nilai koefisien termal terendah pada temperatur 26°C. Sampel hasil sintesis juga diuji sifat mekaniknya dengan menggunakan instrumen Uji Tarik tensile strength yang menunjukkan nilai perpanjangan modulus elastisitas tinggi dihasilkan oleh penggunaan surfaktan Disponil A 1080 ================================================================================================= Synthesis of methanol-based PVAc have been successfully conducted using vinyl acetate monomer and use variations of some surfactants namely Disponil FES IS 27; Disponil A 1080; Disponil AES 72; AFX Disponil 3070. This research was conducted with emulsion polymerization process using a specially designed glass reactor for polymerization reactions. Product was analyzed by Fourier Transform Infrared (FTIR), indicating that there is no influence of surfactants on the formation of functional groups in product, evidenced by the spectra are same at all. Surfactant Disponil AFX had large viscosity from the others. Analyzed using Thermomechanical Analysis (TMA) shows that the best results obtained from surfactants Disponil A 1080 with lowest thermal coefficient on temperature 26°C. The product is also tested the mechanical property by using the tensile strength instrument that shows surfactants Disponil A 1080 had high expansion and modulus elasticity

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 547.28 Ama s
Uncontrolled Keywords: Polimerisasi emulsi, Monomer Vinyl Asetat, Pengaruh Surfaktan
Subjects: Q Science > QD Chemistry > Polymerization
Divisions: Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 22 Oct 2020 09:01
Last Modified: 22 Oct 2020 09:01
URI: https://repository.its.ac.id/id/eprint/82186

Actions (login required)

View Item View Item