Studi Pengaruh Kecepatan Pengadukan Terhadap Morfologi dan Sifat Termal Mikrokapsul Polisulfon Berbasis Minyak Tung Sebagai Self-Healing Coating

Salsah, Rizka Putri (2021) Studi Pengaruh Kecepatan Pengadukan Terhadap Morfologi dan Sifat Termal Mikrokapsul Polisulfon Berbasis Minyak Tung Sebagai Self-Healing Coating. Undergraduate thesis, Institut Teknology Sepuluh Nopember.

[img] Text
02511740000026-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only until 1 April 2023.

Download (4MB) | Request a copy

Abstract

Korosi adalah kerusakan pada logam karena adanya reaksi dengan lingkungannya. Salah satu cara pencegahan korosi yang sering digunakan adalah dengan cara coating. Penelitian ini bertujuan membuat mikrokapsul polisulfon berbasis minyak tung dan menganalisis pengaruh dari kecepatan pengadukan terhadap morfologi dan sifat termal mikrokapsul sebagai self-healing coating. Metode yang digunakan dalam penelitian ini adalah mikroenkapsulasi solvent evaporation method. Polisulfon dipilih sebagai material cangkang karena mempunyai sifat stabilitas termal dan ketahanan kimia yang baik. Minyak tung dipilih sebagai material inti karena mempunyai sifat stabilitas termal dan viskositas yang baik, serta dapat meminimalisir terjadinya korosi. Variasi yang digunakan pada tugas akhir ini adalah variasi kecepatan pengadukan 500, 700, 900, 1100 rpm. Hasil analisis FTIR mengkonfirmasi terjadinya enkapsulasi pada variasi mikrokapsul. Pengamatan secara visual menggunakan mikroskop optik menunjukkan bahwa terlihat adanya penurunan diameter mikrokapsul seiring dengan peningkatan kecepatan pengadukan dan peningkatan jumlah mikrokapsul terbanyak pada 1100 rpm. Hasil analisis SEM menunjukkan terjadi penurunan kekasaran mikrokapsul, dan hasil analisis TGA menunjukkan mikrokapsul stabil hingga temperatur 340oC dan berhasil dienkapsulasi dengan kapasitas enkapsulasi sebesar 51,6%. ====================================================================================================== Corrosion is failure of metal due to reactions with their environment. One way to prevent corrosion that is often used is coating. The aim of this study were to make polysulfone microcapsules based on tung oil and analyze the effect of stirring speed on the morphology and thermal property microcapsules as a self-healing coating. In this study the microencapsulation method used was solvent evaporation method. Polysulfone was chosen as the shell material because it has good thermal stability and chemical resistance properties. Tung oil was chosen as the core material because it has good thermal stability and viscosity properties, and can minimize corrosion. The variation used in this study was variation of stirring speed at 500, 700, 900, 1100 rpm. The result of FTIR analysis confirmed the encapsulation of the various microcapsules. Visual observations using an optical microscope showed that there was a decrease in the diameter of the microcapsules along with the increase in stirring speed and the most number of microcapsules increase at 1100 rpm. SEM analysis results showed a decrease in microcapsule roughness, and the results of TGA analysis showed that the microcapsules were stable up to a temperature of 340oC and successfully encapsulated with capacity of encapsulation is 51.6%.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Mikrokapsul, Mikroenkapsulasi, Minyak Tung, Polisulfon, Self-Healing Coating
Subjects: Q Science > QD Chemistry > QD79.T38 Thermal analysis
T Technology > TA Engineering (General). Civil engineering (General) > TA418.9.C57 Coatings
T Technology > TP Chemical technology > TP1140 Polymers
T Technology > TP Chemical technology > TP669 Oils, fats, and waxes
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Rizka Putri Salsah
Date Deposited: 22 Feb 2021 08:13
Last Modified: 22 Feb 2021 08:13
URI: https://repository.its.ac.id/id/eprint/82700

Actions (login required)

View Item View Item