Pengaruh Pelarut Terhadap Morfologi Komposit H-ZSM-5-TIO2 Termodifikasi Karbon

Indrawan, Andy Kusuma (2021) Pengaruh Pelarut Terhadap Morfologi Komposit H-ZSM-5-TIO2 Termodifikasi Karbon. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
01211540000111-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only until 1 April 2023.

Download (1MB) | Request a copy

Abstract

Komposit ZSM-5-TiO2 termodifikasi karbon telah disintesis dengan metode sol-gel. Prekursor yang digunakan adalah Titanium (IV) Isopropoksida. Variasi pelarut yang digunakan adalah isopropanol, benzena dan toluena. Hasil sintesis dikarakterisasi dengan FTIR, XRD, dan SEM. Hasil karakterisasi XRD menunjukkan puncak karakteristik TiO2 muncul pada 2θ = 25,3°; 37,8°; dan 48,2°. Hasil karakterisasi FTIR menunjukan pita serapan dari IZTC, B-ZTC, dan T-ZTC yang serupa dengan pita serapan ZSM-5 di sekitar bilangan gelombang 3464, 1639, 1222, 1097, dan 545 cm-1. Hasil FTIR juga menunjukkan pita serapan di sekitar bilangan gelombang 450 cm-1 yang menunjukkan vibrasi ulur TiO. Hasil karakterisasi SEM-EDX menunjukkan persebaran Ti lebih merata pada permukaan T-ZTC dibandingkan B-ZTC dan I-ZTC. Hal tersebut menunjukkan kepolaran pelarut mempengaruhi persebaran TiO2. Pelarut yang kepolarannya lebih rendah menunjukkan persebaran TiO2 yang lebih merata. Toluena adalah pelarut yang memiliki persebaran TiO2 paling merata untuk sintesis H-ZSM-5-TiO2 termodifikasi karbon. ===================================================================================================== Carbon-modified H-ZSM-5-TiO2 composite was synthesized by sol-gel method. The precursor used was Titanium (IV) Isopropoxide. The solvents were varied by using isopropanol, benzene and toluene. To determine the effect of varied solvents on composite’s morphology, characterizations using FTIR, XRD, and SEM have been used. The results of XRD has shown that TiO2 peak characteristic were identified at 2θ = 25,3°; 37,8°; dan 48,2°. The results of FTIR has shown that I-ZTC, B-ZTC, and T-ZTC has similar absorbtion bands with ZSM-5 at 3464, 1639, 1222, 1097, dan 545 cm-1. The results of FTIR also shown that I-ZTC, B-ZTC and T-ZTC has absorption bands around wavelength 450 cm-1 which shown the stretching vibration of Ti-O bond. The results of SEM-EDX has shown that Ti were more equally dispersed on the surface of T-ZTC than B-ZTC and I-ZTC. It was shown that polarity of solvent affects the dispersion of TiO2. Solvent with lower polarity has shown better dispersion of TiO2. Toluene is better solvent for the synthesis of carbon-modified H-ZSM-5-TiO2 in term of TiO2 dispersion.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Morfologi, komposit, ZSM-5, TiO2, persebaran morphology, composite, ZSM-5, TiO2, dispersion
Subjects: Q Science > QD Chemistry > QD716 Photocatalysis.
Divisions: Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Indrawan Andy Kusuma
Date Deposited: 09 Mar 2021 08:54
Last Modified: 09 Mar 2021 08:55
URI: https://repository.its.ac.id/id/eprint/83432

Actions (login required)

View Item View Item