Peningkatan Ketahanan Degradasi Paduan Magnesium AZ31B Yang Dilapisi Hidroksiapatit Menggunakan Metode Plasma ELectrolytic Oxidation (PEO) dan Electrophoretic Deposition(EPD)

Rohmah, Amilatin (2021) Peningkatan Ketahanan Degradasi Paduan Magnesium AZ31B Yang Dilapisi Hidroksiapatit Menggunakan Metode Plasma ELectrolytic Oxidation (PEO) dan Electrophoretic Deposition(EPD). Masters thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
02511850010006-Master_Tesis.pdf
Restricted to Repository staff only

Download (7MB) | Request a copy

Abstract

Belakangan ini banyak penelitian yang mengembangkan magnesium sebagai implan tulang karena magnesium merupakan salah satu unsur yang diperlukan didalam tubuh. Magnesium memiliki sifat mekanik yang hampir sama dengan tulang, tetapi laju degradasi dari magnesium berlangsung cepat. Teknologi rekayasa permukaan diperlukan untuk menurunkan laju degradasi pada substrat magnesium. Pada penelitian ini menggunakan teknologi rekayasa permukaan Plasma Electrolytic Oxidation (PEO) dan Electrophoretic Deposition (EPD), larutan elektrolit yang digunakan pada saat proses PEO adalah KOH dan Na3PO4.12H2O. Konsentrasi KOH yang digunakan adalah 1g/l, sedangkan konsentrasi dari Na3PO4.12H2O divariasikan yaitu 0,5, 1, dan 2,26 g/l. Setelah proses pelapisan PEO kemudian dilanjutkan dengan EPD menggunakan suspensi yang ditambahkan hidroksiapatit. Konsentrasi hidroksiapatit yang digunakan bervariasi yaitu 3 g/l, 5g/l, dan 10g/l. Dari hasil Uji XRD didapatkan terbentuknya senyawa Mg dan Mg3(PO4)2, dan dari pengamatan menggunakan SEM terlihat morfologi permukaan lapisan dengan mikropori. Pada saat konsentrasi Na3PO4.12H2O naik sampai 2,26 g/l pori yang terbentuk semakin besar, merata dan padat. Hasil dari pengujian SEM lapisan PEO/EPD terlihat bahwa hidroksiapatit berhasil menutup mikropori. Semakin banyak konsentrasi hidroksiapatit dalam suspensi maka semakin banyak pori yang tertutup, namun untuk pori dengan ukuran lebih besar belum bisa tertutup sempurna. Dari uji potensiodinamik bahwa pelapisan PEO/EPD dapat menghambat laju korosi dari magnesium AZ31B dari 50,219 mmpy menurun menjadi sebesar 0,001 mmpy pada saat konsentrasi hidroksiapatitnya 10g/l. Dari hasil uji imersi pada larutan SBF didapatkan bahwa dengan pelapisan PEO/EPD dapat menurunkan laju degradasi dari paduan magnesium AZ31B dari 0,1126 mmpy menjadi 0,0126 mmpy. ================================================================================================ Recently, most studies about biodegradable magnesium. Magnesium one of the candidate materials for implant application because magnesium is a necessary element in the body and has the same mechanical properties as human bone, but the degradation rate of magnesium fast. The surface treatment is required to decrease the degradation rate on magnesium substrates. This study using Plasma Electrolytic Oxidation (PEO) and Electrophoretic Deposition (EPD). The electrolyte solution of PEO used was KOH and Na3PO4.12H2O. The KOH concentration is 1g/l, and Na3PO4.12H2O concentration was varied 0.5, 1, and 2.26g/l. After the PEO coating process was followed by EPD using suspension with adding hydroxyapatite. The hydroxyapatite concentrations used varied, namely 3 g/l, 5g/l, and 10g/l. XRD analysis, it was found MgO and Mg3(PO4)2 and the SEM result that micropore on the surface coating. When the Na3PO4.12H2O concentration is increased until 2.26g/l the pores are homogenous, dense, and large. The SEM result of PEO/EPD coating showed that the hydroxyapatite success closes the micropores. The concentration of hydroxyapatite is increasing, the more micropores are closed, but large pores cannot be completely closed. From the potentiodynamic polarization test results, the PEO/EPD coating can decrease the corrosion rate of magnesium AZ31B from 50.219 mmpy to 0.001 mmpy. From immersion testing on SBF solution result that PEO/EPD coating can decrease the degradation rate of magnesium AZ31B from 0.1126 mmpy to 0.0126 mmpy

Item Type: Thesis (Masters)
Uncontrolled Keywords: Magnesium AZ31B, Plasma Electrolytic Oxidation (PEO), Magnesium AZ31B, Plasma Electrolytic Oxidation (PEO), Tri-sodium Fosfat, Electrophoretic Deposition(EPD), Hydroxyapatit,Tri-sodium Fosfat, Electrophoretic Deposition(EPD), Hidroksiapatit
Subjects: T Technology > T Technology (General) > TA404 Materials--Biodegradation
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 27101-(S2) Master Thesis