Studi Pengaruh Struktur Filler Serat Pisang Abaca (Pendek, Panjang, dan Anyam) Sebagai Material Absorber yang Ramah Lingkungan

Fitriani, Syangidah Septi (2021) Studi Pengaruh Struktur Filler Serat Pisang Abaca (Pendek, Panjang, dan Anyam) Sebagai Material Absorber yang Ramah Lingkungan. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
01111640000030-Undergraduate_Thesis.pdf
Restricted to Repository staff only

Download (2MB) | Request a copy

Abstract

Penelitian ini dilakukan untuk mengetahui pengaruh dari struktur filler serat pisang abaca (pendek, panjang, dan anyam) terhadap nilai koefisien absorbsi bunyi dan insertion loss. Pengukuran dilakukan dengan menggunakan tabung impedansi. Pengujian yang dilakukan adalah pengujian densitas, morfologi, koefisien absorbsi, dan insertion loss. Hasil pengujian koefisien absorbsi menunjukkan bahwa sampel E memiliki nilai tertinggi yaitu sebesar 0,94 pada frekuensi 1000 Hz. Dan pada hasil pengujian insertion loss didapatkan nilai tertinggi sebesar 25,31 dB pada sampel 1 pada frekuensi 2000 Hz. Rentang nilai insertion loss yang didapatkan adalah antara 10,87-25,31 dB, dan grafik yang ditunjukkan hampir sama, ini dikarenakan sampel memiliki ketebalan yang sama. Massa menjadi salah satu faktor yang mempengaruhi nilai dari insertion loss. Dari hasil yang didapatkan, variasi struktur filler serat pisang abaca pada sampel yang digunakan tidak mengalami pengaruh yang signifikan. Hal ini dikarenakan komposisi yang digunakan dalam komposit lebih didominasi oleh matriks daripada filler. Perlu dilakukan penelitian selanjutnya dengan komposisi filler yang lebih banyak untuk dapat mengetahui pengaruh struktur filler serat pisang abaca, dan perlu dilakukan proses molding yang lebih baik. ========================================================================================== This research was conducted to determine the effect of the abaca fiber filler structure (short, long, and woven) on the sound absorption coefficient and insertion loss. Measurements are made using an impedance tube. The tests performed were density, morphological, absorption coefficient and insertion loss testing. The result of the absorption coefficient test showed that the sample E had the highest value of 0,94 at a frequency of 1000 Hz. And the insertion loss test results obtained the highest value of 25,31 dB in sample 1 at a frequency 2000 Hz. The range of insertion loss values obtained is between 10,87-25,31 dB, and the graph shown is almost the same, this is because the samples have the same thickness. Mass is one of the factors that influence the value of insertion loss. From the results obtained, the variation of the abaca fiber filler structure in the sample used did not experience a significant effect. This is because the composition used in the composites is dominated by a matrix rather than a filler. It is necessary to carry out further research with more filler compositions to be able to determine the effect of the abaca fiber filler structure.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: absorber, absorption coefficient, insertion loss, absorber, insertion loss, koefisien absorbsi
Subjects: Q Science > QC Physics > QC221 Acoustics. Sound
Divisions: Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User: SYANGIDAH SEPTI FITRIANI
Date Deposited: 06 Mar 2021 03:54
Last Modified: 06 Mar 2021 03:54
URI: https://repository.its.ac.id/id/eprint/83584