Pengaruh Variasi Media Pendingin Annealing Pada CuZn35 Terhadap Sifat Mekanik Dan Struktur Mikro Untuk Aplikasi Selongsong Peluru

Agustin, Wahyu (2021) Pengaruh Variasi Media Pendingin Annealing Pada CuZn35 Terhadap Sifat Mekanik Dan Struktur Mikro Untuk Aplikasi Selongsong Peluru. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

Text 02511740000004-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2023. Download (1MB) | Request a copy

Abstract

Dengan semakin tingginya kebutuhan selongsong peluru di Indonesia mendorong diperlukannya riset untuk memperoleh material alternatif. Salah satu material alternatif tersebut adalah CuZn35. Untuk mendapatkan spesifikasi material yang sesuai sebagai bahan selongsong yaitu CuZn30, maka diperlukan perlakuan panas annealing pada CuZn35 dengan variasi media pendingin furnace, udara, air dan air es untuk dianalisis pengaruhnya terhadap sifat mekanik dan struktur mikro untuk aplikasi deep drawing pada selongsong peluru. Selanjutnya dilakukan pengujian tarik, kekerasan, XRD, metalografi dan proses deep drawing. Dari hasil pengujian yang telah dilakukan, struktur mikro yang dihasilkan adalah fasa alpha. Semua spesimen berhasil dilakukan deep drawing tahap pertama tanpa menimbulkan keretakan. Dari keseluruhan spesimen yang memenuhi nilai target UTS, YS, elongasi dan kekerasan sesuai target CuZn30 adalah spesimen media pendingin furnace dengan nilai UTS sebesar 319 MPa, nilai YS sebesar 103 MPa, nilai elongasi sebesar 64,94% dan nilai kekerasan sebesar 71,26 VHN.
==============================================================================================
Research on alternative materials such as CuZn35 is needed due to the increasing demand for cartridge cases in Indonesia. To get a suitable material as the standard CuZn30 cartridge cases, an annealing treatment of CuZn35 through various cooling media such as a furnace, air, water, and ice water to analyze its effect on mechanical properties and microstructure for deep drawing applications on the cartridge case. Furthermore, tensile tests, hardness tests, XRD, metallography, and deep drawing processes were carried out. The result shows that the first stage of the deep drawing process was carried out without causing cracks. Out of all specimens, the specimens with furnace cooling media were the only specimens that met all the CuZn30 standard requirements in terms of UTS 319 MPa, YS 103 MPa, elongation 64,94%, and hardness 71,26 VHN.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	Annealing, CuZn35, deep drawing, media pendingin, selongsong, Annealing, Cartridge case, Cooling media, CuZn35, Deep drawing
Subjects:	T Technology > TS Manufactures > TS205 Metals--Heat treatment.
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering
Depositing User:	Wahyu Agustin
Date Deposited:	11 Aug 2021 05:15
Last Modified:	11 Aug 2021 05:15
URI:	http://repository.its.ac.id/id/eprint/85839