Analisis Pengaruh Silane Coupling Agent dan Rasio Porogen terhadap Morfologi, Sifat Mekanik, dan Biodegradasi 3D Scaffolds Komposit PLGA/Nano-Hidroksiapatit

Deyastama, Muhammad Daffarif (2021) Analisis Pengaruh Silane Coupling Agent dan Rasio Porogen terhadap Morfologi, Sifat Mekanik, dan Biodegradasi 3D Scaffolds Komposit PLGA/Nano-Hidroksiapatit. Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[thumbnail of 02511740000049-Undergraduate_Thesis.pdf] Text
02511740000049-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Registered users only until 1 October 2023.

Download (3MB) | Request a copy

Abstract

Beberapa penelitian sedang mengembangkan solusi untuk permasalahan fraktur tulang, salah satunya dengan sintesis material komposit sebagai material scaffold. Penelitian ini menggunakan bahan Poly(lactic-co-glycolic) sebagai matriks dan nano-hidroksiapatit yang dimodifikasi dengan silane coupling agent sebagai filler. Metode sintesis yang digunakan adalah Solvent Casting/Particulate Leaching (SCPL) dengan porogen NaCl. Tujuan dari penelitian ini adalah menganalisis variasi penambahan 1, 3, dan 5% silane coupling agent APTES dan variasi rasio porogen NaCl terhadap polimer 4:1, 6:1, dan 8:1 terhadap morfologi, sifat mekanik, dan biodegradasi komposit PLGA/Nano-Hidroksiapatit. Pengujian yang dilakukan adalah Digital Microscope dengan bantuan software ImageJ untuk menganalisis morfologi dan porositas. FTIR untuk menganalisis ikatan antara silane coupling agent dan nano-hidroksiapatit. Pengujian tarik dan tekan untuk menganalisis sifat mekanik komposit 3D scaffolds. Pengujian weight loss menggunakan larutan Phosphate Buffered Saline selama 15 hari untuk menganalisis biodegradasi dan memprediksi life time dari komposit 3D scaffolds. Hasil terbaik dimiliki oleh biokomposit variasi 3% APTES dengan 6:1 antara NaCl dengan polimer dengan nilai 76,623% porositas, variasi 3% APTES dengan 4:1 antara NaCl dengan polimer dengan nilai uji tarik sebesar 0,85MPa, variasi 5% APTES dengan 6:1 antara NaCl dengan polimer dengan nilai uji tekan sebesar 6,013, dan variasi 3% APTES dengan 4:1 antara NaCl dengan polimer dengan lifetime degradasi sebesar 20,33 bulan.
===================================================================================================
Several studies are developing solutions for bone fracture problems, one of which is the synthesis of composite materials as scaffold materials. This research uses Poly(lactic-co-glycolic) as a matrix and modified nano-hydroxyapatite with silane coupling agent as a filler. The synthesis method used is Solvent Casting/Particulate Leaching with NaCl as porogen. The purpose of this study was to analyze variations of 1, 3, 5% silane coupling agent and variations in the ratio of porogen NaCl to polymer 4:1, 6:1, 8:1 on morphology, mechanical properties and biodegradation of PLGA/Nano-Hydroxyapatite composites. The tests in this study were Digital Microscope with help of ImageJ software to analyze morphology and porosity. FTIR to validate the bond between silane coupling agent and nano-hydroxyapatite. Tensile and compressive testing to analyze the properties of 3D scaffolds composites. The weight loss test used Phosphate Buffered Saline solution to analyze biodegradation and predict the life time of the 3D scaffolds composite. The best results were obtained by biocomposite PLGA/nHAp/N6/A3% with a porosity value 76,623%, PLGA/nHAp/N4/A3% with a tensile test value 0,85MPa, PLGA/nHAp/N6/A5% with a compressive test value of 6,013MPa, dan PLGA/nHAp/N4/A3% with a lifetime degradation of 20,33 months.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Hidroksiapatit, PLGA, SCPL, Silane Coupling Agent, Tulang
Subjects: Q Science
Q Science > QC Physics > QC173.4.C63 Composite materials
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Muhammad Daffarif Deyastama
Date Deposited: 14 Aug 2021 02:57
Last Modified: 14 Aug 2021 02:57
URI: http://repository.its.ac.id/id/eprint/86199

Actions (login required)

View Item View Item