Green Synthesis Seng Oksida (ZnO) Menggunakan Ekstrak Daun Waru (Hibiscus Tiliaceus L.) Untuk Degradasi Fotokatalisis Zat Warna

Syafdhani, Haritsa (2021) Green Synthesis Seng Oksida (ZnO) Menggunakan Ekstrak Daun Waru (Hibiscus Tiliaceus L.) Untuk Degradasi Fotokatalisis Zat Warna. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
01211740000033-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only until 1 October 2023.

Download (2MB)

Abstract

Dengan bertambahnya zaman, biosintesis partikel menjadi bidang penelitian yang menarik disebabkan pengaplikasiannya yang luas. Tujuan utama dari makalah ini adalah pembuatan partikel seng oksida (ZnO) menggunakan metode green synthesis dari ekstrak daun waru (Hibiscus tiliaceus L.) dengan variasi etanol dan air pada pelarut ekstrak. Selanjutnya seng oksida (ZnO) yang dihasilkan dikarakterisasi meliputi analisis gugus fungsi menggunakan instrumen FTIR, morfologi permukaan menggunakan instrumen SEM dan mengetahui jenis fasa menggunakan instrumen XRD (X-ray Diffraction). Hasil penelitian menunjukan green synthesis seng oksida (ZnO) menggunakan ekstrak daun waru (Hibiscus tiliaceus L.) memiliki distribusi ukuran partikel 0,5 µm hingga 0,75 µm. Degradasi fotokatalisis menggunakan seng oksida hasil green synthesis dapat menghilangkan lebih dari 90% metilen biru dalam waktu 75 menit. ================================================================================================ Recently, biosynthesis of particles is an exciting area of research with wide applications. The main objective of this paper is making zinc oxide particles using the green synthesis method from Hibiscus tiliaceus L. extract with variations of ethanol and water in the extract solvent. Furthermore, zinc oxide products were characterized using FTIR for functional group analysis, SEM for surface morphology and XRD for find out its phase. The results showed green synthesis zinc oxide using Hibiscus tiliaceus L. extract had a particle size distribution of 0,5 μm to 0,75 μm. Photocatalytic degradation using green synthesis zinc oxide can remove more than 89% of methylene blue in 75 minutes.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Fotokatalisis, Green Synthesis, Seng Oksida, dan Daun Waru (Hibiscus tiliaceus L.) Photocatalytic, Zinc Oxide and Hibiscus tiliaceus L.
Subjects: Q Science
Q Science > QD Chemistry
Q Science > QD Chemistry > QD716 Photocatalysis.
Divisions: Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Haritsa Syafdhani
Date Deposited: 20 Aug 2021 18:56
Last Modified: 20 Aug 2021 18:56
URI: https://repository.its.ac.id/id/eprint/88165

Actions (login required)

View Item View Item