Sintesis Zeolit NaY Dari Kaolin Dengan Perlakuan Asam Sulfat Dan Modifikasi Dengan Ni Untuk Hidrogenasi CO2 Menjadi Metana

Sholeha, Novia Amalia (2021) Sintesis Zeolit NaY Dari Kaolin Dengan Perlakuan Asam Sulfat Dan Modifikasi Dengan Ni Untuk Hidrogenasi CO2 Menjadi Metana. Doctoral thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
01211860010006-Dissertation.pdf - Accepted Version
Restricted to Repository staff only until 1 October 2023.

Download (6MB) | Request a copy

Abstract

Zeolit NaY telah berhasil disintesis dari kaolin Bangka sebagai material pendukung logam Ni. Kaolin yang telah diaktivasi secara termal diberikan beberapa perbedaan perlakuan yakni penambahan asam sulfat (SM), pencucian dengan H2O (DM) serta tanpa penambahan perlakuan (M) sebagai pembanding. Penelitian ini bertujuan untuk mengetahui pengaruh perlakuan asam sulfat pada sifat tekstural zeolit NaY sebagai material pendukung Ni pada reaksi hidrogenasi CO2 menjadi CH4. Sintesis NaY dilakukan dengan metode hidrotermal pada suhu 100 °C dengan rasio molar 6 Na2O: 10 SiO2: Al2O3: 180 H2O. Inkoporasi logam Ni pada material NaY hasil sintesis dilakukan dengan metode impregnasi. Padatan yang terbentuk dikarakterisasi XRD, FTIR, adsorpsi-desorpsi N2, SEM, dan HRTEM. Hasil karakterisasi menunjukkan bahwa zeolit NaY-DM memiliki kristalinitas tertinggi dan morfologi yang teratur jika dibandingkan NaY-M dan NaY-SM. Luas permukaan yang lebih tinggi pada zeolit NaY-DM sebesar 505 m2/g membuat dispersi logam Ni lebih merata dan ukuran rata-rata partikel NiO yang lebih kecil (18 nm). NaY-DM juga memiliki Si/Al yang meningkat menjadi 1,32. Adanya penambahan luas permukaan dan rasio Si/Al meningkatkan konversi CO2 menjadi 67%. ======================================================================================================= NaY zeolite has been successfully synthesized from Bangka kaolin as support material for Ni metal. Thermally activated kaolin was given several different treatments i.e., sulfuric acid addition (SM), H2O washing (DM), and no treatment (M) as comparison. This research aimed to study the effect of sulfuric acid treatment on the texture properties of NaY zeolite as supporting material for Ni in the reaction of CO2 hydrogenation to CH4. The synthesis of NaY was carried out by hydrothermal method at 100 °C with molar ratio of 6 Na2O: 10 SiO2: Al2O3: 180 H2O. The incorporation of Ni metal into the synthetic NaY material was carried out by the impregnation method. The solids were characterized by XRD, FTIR, N2 adsorption-desorption, SEM, and HRTEM. The characterization results showed that NaY-DM zeolite had the highest crystallinity and regular morphology when compared to NaY-M and NaY-SM. The higher surface area of the NaY-DM zeolite of 505 m2/g made the Ni metal more dispersed and smaller average NiO particle size (18 nm). NaY-DM also has increased Si/Al to 1.32. The increasing of surface area and Si/Al ratio results in higher CO2 conversion to 67%.

Item Type: Thesis (Doctoral)
Uncontrolled Keywords: NaY, metakaolin, asam sulfat, pencucian, konversi CO2, logam Ni, NaY, metakaolin, sulfuric acid, washing, CO2 conversion, Ni metal
Subjects: Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
T Technology > TN Mining engineering. Metallurgy > TN271.K2 Kaolin
T Technology > TP Chemical technology > TP159.M6 Zeolites
Divisions: Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47001-(S3) PhD Thesis
Depositing User: Novia Amalia Sholeha
Date Deposited: 22 Aug 2021 03:19
Last Modified: 22 Aug 2021 03:19
URI: https://repository.its.ac.id/id/eprint/88628

Actions (login required)

View Item View Item