Sintesis Katalis Al-MCM-41 dari Red Mud dan Aplikasinya pada Reaksi Deoksigenasi Minyak Kemiri Sunan

Zendasary, Afna Agata (2021) Sintesis Katalis Al-MCM-41 dari Red Mud dan Aplikasinya pada Reaksi Deoksigenasi Minyak Kemiri Sunan. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
01211740000005-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only until 1 October 2023.

Download (2MB) | Request a copy

Abstract

Sintesis katalis Al-MCM-41 dari red mud dan aplikasinya untuk reaksi deoksigenasi minyak kemiri sunan telah berhasil dilakukan. Katalis Al-MCM-41 disintesis menggunakan metode hidrotermal dua tahap dengan penambahan CTABr sebagai pengarah mesopori. Katalis yang telah disintesis selanjutnya dikalsinasi pada suhu 550°C dengan aliran N2 (laju aliran 2°C /menit) selama 1 jam dan aliran udara selama 6 jam. Uji aktivitas katalitiknya dilakukan dengan reaksi deoksigenasi minyak kemiri sunan pada reaktor semi-batch selama 4 jam dengan suhu 350°C. Hasil karakterisasi XRD pada katalis Al-MCM-41 menunjukkan struktur khas amorf Al-MCM-41 dan hasil analisa FTIR menunjukkan vibrasi molekul yang sesuai dengan ciri-ciri Al-MCM-41. Analisa adsorpsi desorpsi nitrogen dilakukan untuk mengetahui struktur hexagonal mesopore dari Al-MCM-41. Katalis ini memiliki luas permukaan total 461,37 m2/g dengan sisi mesopori 84,35 m2/g. Morfologi dari katalis Al-MCM-41 menunjukkan adanya aglomerasi dari kristal kecil menjadi agregat yang lebih besar dengan ukuran partikel 0,6 – 1,4 μm. Katalis Al-MCM-41 terdiri dari elemen Al, Si, Fe dan O dengan kadarnya secara berurutan adalah 5,45%, 39,61%, 2,72%, 49,09%. Hasil analisa GC-MS pada produk deoksigenasi dengan katalis tersebut menunjukkan selektivitas hidrokarbon sebesar 48,5% dengan distribusi rantai karbon pada range hidrokarbon rantai pendek C6-10 dan hidrokarbon rantai panjang C11-17. ======================================================================================================= The synthesis of Al-MCM-41 catalyst from red mud for deoxygenation of Reutealis trisperma was successfully done. The synthesis of Al-MCM-41 was carried out via two-step hydrothermal using CTABr as mesopore template. Then, the catalyst was calcined at 550°C under N2 flow (flow rate of 2°C/min) for 1 h followed by air flow for 6 h. The catalytic activity was analyzed by deoxygenation of Reutealis trisperma using semi-batch reactor for 4 h at 350°C. Based on the result of XRD, the catalyst showed an amorphous structure indicating the characteristic of Al-MCM-41. On the other hand, the result of FTIR showed the same vibration molecules as the characteristic of Al-MCM-41. The hexagonal mesopore structure of Al-MCM-41 was analyzed by adsorption-desorption nitrogen. This catalyst has a total surface area of 461,37 m2/g with a mesopore area of 84,35 m2/g. The morphology of Al-MCM-41 showed an agglomeration of small crystallite with 0,6 – 1,4 μm particle size. The Al-MCM-41 catalyst consist of Al, Si, Fe and O element which have value 5,45%, 39,61%, 2,72%, 49,09% respectively. Then, the selectivity of the catalyst was analyzed by GC-MS of the liquid product. The catalyst resulting 48,5% selectivity of hydrocarbon with range of hydrocarbon chain between C6-C10 and C11-C17.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Red mud, Al-MCM-41, Reutealis trisperma, Deoksigenasi Red mud, Al-MCM-41, Reutealis trisperma, Deoxygenation
Subjects: Q Science
Q Science > QD Chemistry
Q Science > QD Chemistry > QD181.S6 A4 Aluminum silicates
Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Depositing User: Afna Agata Zendasary
Date Deposited: 22 Aug 2021 03:21
Last Modified: 22 Aug 2021 03:21
URI: https://repository.its.ac.id/id/eprint/89616

Actions (login required)

View Item View Item