PENGARUH KECEPATAN PUTAR, GAYA GESEK, WAKTU GESEK TERHADAP KEKERASAN, KEKUATAN IMPAK, LAJU KOROSI DAN STRUKTUR MIKRO HASIL LASAN PROSES LAS GESEK MATERIAL BERBEDA BAJA SUH 3 DAN SUH 35

Sai'in, Ali (2016) PENGARUH KECEPATAN PUTAR, GAYA GESEK, WAKTU GESEK TERHADAP KEKERASAN, KEKUATAN IMPAK, LAJU KOROSI DAN STRUKTUR MIKRO HASIL LASAN PROSES LAS GESEK MATERIAL BERBEDA BAJA SUH 3 DAN SUH 35. Other thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2114201003-Master_Theses (S2).pdf]
Preview
Text
2114201003-Master_Theses (S2).pdf - Published Version

Download (7MB) | Preview
[thumbnail of 2114201003-Abstract.pdf]
Preview
Text
2114201003-Abstract.pdf - Published Version

Download (180kB) | Preview
[thumbnail of 2114201003-Conclusion.pdf]
Preview
Text
2114201003-Conclusion.pdf - Published Version

Download (158kB) | Preview

Abstract

Las gesek merupakan salah satu teknologi pengelasan yang digunakan untuk menyambung dua material tanpa menggunakan bahan pengisi. Penyatuan benda kerja dilakukan dengan memanfaatkan gesekan dan tekanan. Pengaturan parameter proses dalam las gesek ini seperti kecepatan putar, gaya gesek, waktu gesek, gaya tempa dan waktu tempa sangat menentukan keberhasilan proses pengelasan.
Penelitian dilakukan untuk mengamati pengaruh parameter proses, di antaranya kecepatan putar, gaya gesek, dan waktu gesek terhadap kekasaran, kekuatan impak, laju korosi dan struktur mikro pada material yang dilas dengan menggunakan las gesek. Material yang digunakan merupakan material yang mempunyai komposisi kimia yang berbeda, yaitu baja SUH 3 dan SUH 35. Pengelasan dilakukan dengan mesin las gesek tipe FW10NC. Pengujian hasil pengelasan dilakukan dengan menggunakan alat uji kekerasan mikro vikres, alat uji impak jenis charpy, alat uji laju korosi sel tiga elektroda dengan bantuan software NOVA 1.8. Pengamatan struktur mikro dilakukan menggunakan mikroskop optik dan SEM (Scanning Electron Microscope)-EDX
Hasil penelitian menunjukkan bahwa pada proses pengelasan baja SUH 3 dan SUH 35 terjadi perubahan struktur mikro dan perubahan komposisi kimia pada daerah sambungan. Persentase Cr pada kecepatan putar 2500 rpm 14.99% sedangkan pada kecepatan putar 4500 menjadi sebesar 15.82%. Perubahan parameter proses dapat mengubah sifat mekanis dan laju korosi dari sambungan. Pengelasan pada kecepatan putar 4500 rpm, gaya gesek 10 kN dan waktu gesek 1 detik mampu meningkatkan kekerasan dan kekuatan impak paling tinggi serta penurunan laju korosi paling rendah. Kekerasan pada daerah sambungan tercatat sebesar 54.8 HRC, dengan kekuatan impak sebesar 588.39 kJ/m2, dan mampu menurunkan laju korosi sampai 0.051 mm/tahun. ============================================================================ Friction welding
is
one of welding technology that use
d
to join two
materials
without metal filler
.
Friction and pressure was
utilize
d
to join the material.
P
arameters
setting of
friction welding process like
rotation
speed, friction force, friction time,
forging force and forging time
are determining the
success
ful rate of friction welding
process.
The aim of this study is to observe th
e effect of
turning speed, friction force, and
friction time against hardness, impact strength, corrotion rate and microstructure
on weld
metal under friction welding process.
The material used
in this study
is a material that
has a different chemical comp
osition
, which is SUH 3 and SUH 35. Welding process
was done with friction welding machine FW10NC type
. Micro vickers tester was used
to examined hardness value, whereas impact test was examined using charpymethode,
corrotion rate analyzed with three
-
elect
rode cell test equipment with NOVA 1.8
software, while microstructure observation using optical microscope and scaning
electron microscope (SEM)
.
The result of this study shown that there were micro
structure and chemical
composition change at
weld metal
during welding process SUH 3 and SUH 35 Steel.
Cr percentage is 14.99% at 2500 rpm while increases to 15.82% at 450 rpm. Change of
process parameter can change mechanical properties and corrosion rate at the joint
zone. the Welding process at 4500 rpm, fr
iction force 10 kN and friction time at 1
second can maximize hardness and impact force while still minimize the corrosion rate.
Hardness value at joint zone is 54.8 HRC, the friction force is 588.39 kJ/m2 and can
minimize corrosion rate until 0.051 mm/yea
r.

Item Type: Thesis (Other)
Uncontrolled Keywords: las gesek, kekerasan, kekuatan impak, laju korosi, struktur mikro, friction welding, hardness,impact force, corrotion rate, microstructure.
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21101-(S2) Master Thesis
Depositing User: ALI SAI'IN -
Date Deposited: 12 Jan 2017 02:03
Last Modified: 27 Dec 2018 07:31
URI: http://repository.its.ac.id/id/eprint/1158