SINTESA PARTIKEL MnO2 DENGAN TEKNIK ELEKTROKIMIA DALAM SEL MEMBRAN

VISCARINI, VANDA PIRANTY and ROKHIMA, NUR (2015) SINTESA PARTIKEL MnO2 DENGAN TEKNIK ELEKTROKIMIA DALAM SEL MEMBRAN. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2310100017-2310100079-Undergraduate_theses.pdf]
Preview
Text
2310100017-2310100079-Undergraduate_theses.pdf - Published Version

Download (1MB) | Preview

Abstract

Mangan dioksida (MnO2) adalah elektroda yang menarik
untuk desain superkapasitor karena mudah didapat, biaya murah,
toksisitas rendah dan mempunyai rentang tegangan yang lebar.
Kapasitansi spesifik MnO2 secara teori ± 615 F/g. Namun saat
ini, hanya 30% atau bahkan lebih rendah dari nilai teoritis yang
dapat diperoleh. Partikel MnO2 dengan ukuran nano disintesis
untuk meningkatkan kapasitas penyimpanan dan konduktifitas
material tersebut. Sintesa MnO2 dilakukan dengan metode
elektrokimia pada suhu ruang selama 4 jam menggunakan
elektroda karbon dan larutan elektrolit berupa potassium
permanganate (KMnO4) dan potassium hidroksida (KOH) di
mana daerah anoda dan katoda dipisahkan oleh membran nafion.
Untuk memisahkan partikel yang tebentuk dari impurities
dilakukan pengendapan dengan menggunakan centrifuge
kemudian partikel dicuci sampai bersih dari impurities
menggunakan aquadest. Diberikan alkohol pada hasil endapan
supaya tidak menggumpal. Endapan partikel yang terbentuk
kemudian dikeringkan dalam oven. Percobaan ini dilakukan pada
pH larutan 7 - 11 dan variabel tegangan 1 - 5 V. Pada percobaan
dengan menggunakan membran nafion, larutan KMnO4 langsung
dituangkan pada daerah katoda. Sintesis MnO2 menghasilkan
MnO2 untuk superkapasitor yang nilai kapasitansi spesifiknya
lebih besar yaitu 922,67 F/g (α-MnO2) 500.000 kali besar
dibandingkan dengan kapasitor biasa dengan kapasitansi 1,7
mF/g.

============================================================

Manganese dioxide (MnO2) is an attractive electrode
for supercapacitor designs due to its availability, low cost, low
toxicity and wide voltage windows. Specific capacitance of
MnO2 is ± 1380 F/g in theoretical value. At present, only 30%
or even lower of theoretical value can be obtained.
Nanostructure particles MnO2 are synthesized to improve
their storage capacity and conductivity materials. Synthesis of
MnO2 is prepared by electrochemical method in the room
temperature for 3 hours using carbon as electrodes and
potassium permanganate (KMnO4) and potassium hydroxide
(KOH) aselectrolyte solutions. Both of these electrodes are
separated by nafion membrane. Then, MnO2 are separated
from their solution using centrifuge while are rinsed using
distilled water until it turns into clear solution. The cleaned
particles are dried at 100oC in the oven for 24 hours. This
experiments are conducted with variable pH solution 7 – 10
and voltage (1 – 5 V). In using nafion membrane, KMnO4
solution is directly poured in the cathode’s area. The synthetic
of MnO2 give MnO2 for supercapacitor that the value of
specific capacitance is greater than before, about 922,67 F/g (α-MnO2) 500.000x greater than the ordinary capacitor with the capacitance about 1,7 mF/g .

Item Type: Thesis (Undergraduate)
Additional Information: RSK 660.284 24 Vis s
Uncontrolled Keywords: MnO2; Elektrokimia; Superkapasitor
Subjects: T Technology > TP Chemical technology > TP255 Electrochemistry, Industrial.
Divisions: Faculty of Industrial Technology > Chemical Engineering > 24201-(S1) Undergraduate Thesis
Depositing User: Anis Wulandari
Date Deposited: 09 Jan 2017 02:25
Last Modified: 24 Aug 2018 07:19
URI: http://repository.its.ac.id/id/eprint/1387

Actions (login required)

View Item View Item