SINTESIS DAN KARAKTERISASI Ni-ZIF-8

DEDY, YUDIANTO (2014) SINTESIS DAN KARAKTERISASI Ni-ZIF-8. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1409100049-Undergraduate Thesis.pdf] Text
1409100049-Undergraduate Thesis.pdf - Published Version
Restricted to Repository staff only

Download (2MB) | Request a copy

Abstract

Sintesis Ni-ZIF-8 dengan persentase doping logam Ni 0-15%
terhadap logam Zn telah berhasil dilakukan dengan mereaksikan
seng nitrat, nikel klorida dan 2-metilimidazol dalam media DMF
(N’N-dimetilformamida) yang dipanaskan pada suhu 120°C
selama 24 jam. Difraktogram XRD padatan hasil sintesis
menunjukkan puncak-puncak utama pada skitar sudut 2θ = 7,3;
10,3; 12,7; 16,4 dan 18,0°, yang merupakan puncak karakteristik
dari padatan Ni-ZIF-8. Spektra FTIR dari Ni-ZIF-8 hasil sintesis
memiliki puncak serapan pada bilangan gelombang sekitar 421
cm-1 yang menunjukkan adanya ikatan seng dengan nitrogen
dalam Ni-ZIF-8 dan sekitar 1.256 cm-1 yang diduga adalah ikatan
nikel dengan nitrogen. Dari pengukuran dengan metode adsorpsi
N2 diperoleh luas permukaan 1249 m²/g (ZIF-8) dan 1144 m²/g ,
1074 m²/g, 997 m²/g (berturut-turut untuk NiZ-5, NiZ-10 dan
NiZ-15). Hasil analisis termal dengan TGA menunjukkan bahwa
Ni-ZIF-8 hasil sintesis memiliki stabilitas termal pada suhu
hingga 600 °C.

=====================================================================================================

Synthesis of Ni-ZIF-8 has been carried out by reaction of
zinc nitrate, nickel chloride and 2-methylimidazole in DMF (N’Ndimetilformamida)
at 120°C for 24 hours. The difractograms of
materials exhibited strong peaks about at 2θ = 7,3; 10,3; 12,7;
16,4 and 18,0°, which were the characteristic peaks to ZIF-8
materials. Functional group of the Ni-ZIF-8 materials appeared in
the FTIR spectra as a peak at about 410 cm-1 which indicated the
presence of zinc bonded to the nitrogen in Ni-ZIF-8 and about
1.256 cm-1 alleged the presence of nickel bonded to nitrogen in
Ni-ZIF-8. The result of surface area measurement by N2
adsorption method of ZIF-8 was 1249 m²/g (ZIF-8) dan 1144
m²/g , 1074 m²/g, 997 m²/g (respectively for NiZ-5, NiZ-10 dan
NiZ-15). The result of TGA measurement showed that Ni-ZIF-8
had thermal stability in the temperature until 600 °C.

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 548.5 Yud s
Uncontrolled Keywords: Ni-ZIF-8, DMF, karakterisasi
Subjects: Q Science
Q Science > QD Chemistry
Divisions: Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Mr. Tondo Indra Nyata
Date Deposited: 12 Jan 2017 04:03
Last Modified: 22 Jan 2017 22:24
URI: http://repository.its.ac.id/id/eprint/1513

Actions (login required)

View Item View Item