Sintesis K0,5na0,5vo3 Dengan Metode Reaksi Padat, Sifat Dielektrik Dan Potensi Sebagai Cofiring Agent

Sambanyu, Alfian Putra (2016) Sintesis K0,5na0,5vo3 Dengan Metode Reaksi Padat, Sifat Dielektrik Dan Potensi Sebagai Cofiring Agent. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1112100002-undergraduate-theses.pdf]
Preview
Text
1112100002-undergraduate-theses.pdf - Published Version

Download (951kB) | Preview
[thumbnail of 1112100002-paperpdf.pdf]
Preview
Text
1112100002-paperpdf.pdf - Published Version

Download (272kB) | Preview
[thumbnail of 1112100002-presentationpdf.pdf]
Preview
Text
1112100002-presentationpdf.pdf - Published Version

Download (772kB) | Preview

Abstract

Sintesis material K0,5Na0,5VO3 (KNV) telah berhasil dilakukan
dengan metode reaksi padat. Penentuan suhu kalsinasi dan suhu
sintering material ini didasarkan pada titik leleh vanadium oksida
yaitu sekitar 690°C sehingga didapatkan suhu kalsinasi 500°C dan
suhu sintering 500°C dan 525°C selama masing-masing 2 jam. Hal
ini dibuktikan dengan hasil refinement pengujian XRD material
KNV yaitu memiliki fasa tunggal dengan struktur monoklinik dan
grup ruang C2/c. Densitas terukur dari KNV 525 adalah 3,03 g/cc,
sedangkan untuk KNV 500 adalah 3,25 g/cc. Pelet KNV yang telah
disintering kemudian dilakukan pengujian sifat listrik dengan
menggunakan Impedance Analyser “Solartron”. Material KNV
525 dan KNV 500 cocok untuk diaplikasikan sebagai material
dielektrik pada daerah frekuensi yang tinggi. Material KNV 525
memiliki faktor kualitas yang lebih baik daripada KNV 500.
Daerah transisi antara polarisasi muatan ruang dengan polarisasi
dipol untuk KNV 525 berada pada frekuensi 20 kHz, sedangkan
untuk KNV 500 berada pada frekuensi 1,2 MHz. Material KNV
dapat digunakan sebagai co-firing agent pada bahan dielektrik
keramik.
===========================================================
Materials K0.5Na0.5VO3 has been successfully synthesized
by solid state reaction. The calcine and sintering temperature is
based on the melting point of vanadium oxide which is about
690°C, so that we get suitable calcine temperature is 500°C and
sintering temperature is 500°C and 525°C with 2 hours holding
time. It has been proved with the refinement of XRD result that
KNV material has single phase crystal with a monoclinic structure
and C2/c space group. The measuring density for KNV 525 and
KNV 500 sequentially is 3.03 gr/cc and 3.25 gr/cc. To measure
dielectric properties of KNV pellets disc was using Impedance
Analyser “Solartron”. The KNV 500 and KNV 525 is suitable for
high-frequency dielectric material applications. KNV 525 has
better quality factor than KNV 500. The transition area between
space charge polarization and dipole polarization for KNV 525 is
at 20 kHz and 1.2 MHz for KNV 500. The KNV materials can be
use as co-firing agent of dielectric ceramics materials.

Item Type: Thesis (Undergraduate)
Additional Information: RSFi 620.195 Sam s
Uncontrolled Keywords: co-firing agent, dielektrik, reaksi padat, vanadium oksida
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
Divisions: Faculty of Natural Science > Physics > 45201-(S1) Undergraduate Thesis