Pengaruh Penambahan Kitosan Terhadap Sifat Mekanik Komposit Kitosan / Hidroksiapatit Yang Didoping Seng Sebagai Kandidat Material Bone Subtitute

Purnomo, Agus (2016) Pengaruh Penambahan Kitosan Terhadap Sifat Mekanik Komposit Kitosan / Hidroksiapatit Yang Didoping Seng Sebagai Kandidat Material Bone Subtitute. Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[thumbnail of 2712100076-Undergraduate_Thesis.pdf]
Preview
Text
2712100076-Undergraduate_Thesis.pdf - Published Version

Download (4MB) | Preview

Abstract

Komposit Kitosan/HA-Zn telah berhasil dibuat dengan metode
pencampuran basah. Kitosan dengan derajat deasetilasi 84%
dilarutkan dalam asam asetat 3% selama 1 jam pada temperatur 700
C. Kemudian ditambahkan serbuk HA-Zn dengan konsentrasi ion
dopingan sebesar 15 % mol yang dibuat menggunakan metode sol
gel pada temperatur kalsinasi sebesar 9000 C selama 3 jam.
Perbandingan komposisi campuran komposit yakni 10%, 15% dan
20% Kitosan. Hasil serbuk komposit kemudian diuji dengan FTIR,
XRD SEM dan uji densitas untuk karakterisasi sifat fisik. Uji tekan
dan hardness dilakukan untuk mengetahui sifat mekanik. Dari hasil
uji, penambahan Kitosan meningkatkan distribusi ikatan antara
komponen matriks dan filler pada komposit. Penambahan Kitosan
diketahui dapat meningkatkan nilai kekuatan tekan dan nilai
modulus elastisitas serbuk HA-Zn yang dikompositkan. Sedangkan
untuk nilai densitas dan kekerasan permukaan menurun seiring
meningkatnya jumlah Kitosan yang ditambahkan. Sampel
10%K/HA-Zn denan nilai kuat tekan dan modulus elastisitas
masing-masing 57,035 MP dan 0.152 GPa memiliki sifat fisik dan
mekanik yang memenuhi standar sebagai kandidat material
pengganti tulang cancellous
======================================================================= Composite Zinc doped in Chitosan / Hydroxyapatite have been
made with the wet mixing method. Chitosan with degree of
deacetylation of 84% dissolved in 3% acetic acid fisrt for 1 hour at
a temperature of 700 C. Then powder HA-Zn (15% mol Zn) which
created using sol-gel method at calcination temperature of 9000 C
for 3 hours was added. Composition of Chitosan in composite was
10%, 15% and 20%. In this study, characterization of composite
powders has done by FTIR, XRD and SEM. Then test density,
compressive and hardness of compact composite is done to
determine the mechanical properties. In the result, Chitosan
improve the distribution bond between matrix and filler
components of composite. Chitosan increase compressive strength
and modulus elasticity of composite. Furthermore, the density and
surface hardness of composite decreased with increasing the
amount of chitosan. 10%K/HA-Zn with 57,035 MPa of
compressive strength and 0,152 GPa of modulus elasticity, have
the physical and mechanical properties that meet the standards as
cancellous bone substitute material

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.118 Pur p
Uncontrolled Keywords: komposisi, komposit Kitosan/HA-Zn, sifat mekanik, bone subtitute.
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 22 Jan 2020 03:34
Last Modified: 22 Jan 2020 03:34
URI: http://repository.its.ac.id/id/eprint/72866

Actions (login required)

View Item View Item