Karakterisasi Porosity dan Mechanical Properties Al Porous dengan Variasi Temperatur Penuangan

Nurrahman, Fauzan (2021) Karakterisasi Porosity dan Mechanical Properties Al Porous dengan Variasi Temperatur Penuangan. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of Final TA _Muhammad Fauzan Nurrahman_02511740000048.pdf] Text
Final TA _Muhammad Fauzan Nurrahman_02511740000048.pdf - Accepted Version
Restricted to Repository staff only until 1 October 2023.

Download (1MB) | Request a copy
[thumbnail of 02511740000048_Undergraduate-Thesis.pdf] Text
02511740000048_Undergraduate-Thesis.pdf
Restricted to Repository staff only

Download (1MB) | Request a copy

Abstract

Aluminium merupakan logam yang paling banyak digunakan dalam bidang konstruksi dan otomotif. Porositas dapat meningkatkan sifat mekanik dari aluminium dengan memunculkan sifat absorbsi energi yang baik dengan berat dari materialnya yang sangat ringan karena densitasnya yang kecil. Pada penelitian sebelumnya, para peneliti tidak mengidentifikasi apakah pengaruh temperatur penuangan dapat mempengaruhi porositas pada aluminium poros secara spesifik. Pada penelitian ini menggunakan komposisi NaCl dengan jumlah 60 wt.% Al dan variasi pouring temperatur (680, 710, 740) ℃ dengan metode investmen casting untuk menganalisis perbandingan sifat mekanik dan karakterisik al poros dari pengaruh perbedaan temperatur penuangan. Pengujian yang dilakukan untuk melihat perbedaan karakteristik dan sifat mekanik dari aluminium poros adalah pengamatan dengan mikroskop stereo, pengujian densitas dan porositas, kompresi, dan impak yang didapatkan hasil paling optimal pada temperatur 740℃ dengan nilai densitas sebesar 1,66g/cm3 dan persentase porositas 38,16% dengan terdapatnya interconnected pores. Seiring bertambahnya temperatur penuangan persentase porositas naik dan nilai kekuatan kompresi menurun dengan nilai sebesar 51,15MPa, dan nilai absorbsi energi naik dengan nilai sebesar 72,87J.
========================================================================================================
Aluminum is the most widely used metal in the construction
and automotive fields. Porosity can improve the mechanical
properties of aluminum by bringing out good energy absorption properties with a very light weight of the material due to its small density. In previous studies, the researchers did not identify whether the influence of pouring temperature could affect the porosity of the aluminum shaft specifically. In this study, the
composition of NaCl with the amount of 60 wt.% Al and variations of pouring temperature (680, 710, 740) ℃ was used with the investment casting method to analyze the comparison of mechanical properties and porosity characteristics of the effect from different pouring temperatures. The tests carried out to see differences in the characteristics and mechanical properties of al
foam were observed with stereo microscope, density and porosity, compression, and impact testing which obtained the most optimal results at a temperature of 740℃ with the density value of 1.66g/cm3 and the percentage of porosity of 38.16% with the presence of interconnected pores. As the pouring temperature increases the percentage of porosity increases and the value of the compression strength decreases with a value of 51.15MPa, and the energy absorption value increases with a value of 72.87J.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Kata Kunci: Aluminium poros, NaCl, sifat mekanik, porositas, densitas.
Subjects: T Technology > TS Manufactures > TS176 Manufacturing engineering. Process engineering (Including manufacturing planning, production planning)
T Technology > TS Manufactures > TS253 Die-Casting
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Muhammad Fauzan Nurrahman
Date Deposited: 18 Aug 2021 14:02
Last Modified: 18 Aug 2021 14:02
URI: http://repository.its.ac.id/id/eprint/87264

Actions (login required)

View Item View Item