Analisis Pengaruh Penambahan Massa Carbon Quantum Dots (CQDs) dari Limbah Puntung Rokok Terhadap Sifat Fotokatalis Komposit CuO/CQDs untuk Degradasi Methylene Blue

Silaen, Josua Budiman (2024) Analisis Pengaruh Penambahan Massa Carbon Quantum Dots (CQDs) dari Limbah Puntung Rokok Terhadap Sifat Fotokatalis Komposit CuO/CQDs untuk Degradasi Methylene Blue. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5011201017_Undergraduate_Thesis.pdf Download (24MB)

Abstract

Industri tekstil merupakan industri yang akan terus ada dan berkembang seiring dengan majunya teknologi. Salah satu limbah yang berasal dari industri ini adalah pewarna tekstil seperti Methylene Blue. Senyawa ini bersifat toksik, karsinogenik, dan tidak dapat terurai secara alami sehingga perlu diolah sebelum dibuang ke alam. Disisi lain, puntung rokok merupakan salah satu sampah yang banyak ditemukan di dunia. Puntung rokok sebagian besar terbuat dari selulosa asetat yang dapat disintesis menjadi Carbon Quantum Dots (CQDs). CQDs merupakan nanomaterial yang bersifat toksisitas rendah, photoluminescene stabil, serta luas permukaan dapat dimodifikasi dengan fleksibel. Nanomaterial ini dapat diaplikasikan dalam fotokatalis. Semikonduktor CuO memiliki celah pita kecil yakni 1,2 – 2 eV. CQDs bila dikompositkan dengan CuO dapat meningkatkan luas permukaan CuO yang dapat meningkatkan fotokatalis. Metode penelitian ini berfokus pada sintesis CQDs dari puntung rokok dan hasil fotokatalis menggunakan komposit CuO/CQDs dengan penambahan massa CQDs 5%, 15%, 25%, dan 35% dengan massa total 2 gram. Pengujian karakterisasi yang digunakan meliputi XRD, FTIR, SEM/EDX, dan PSA untuk menganalisis struktur, morfologi, ukuran, dan distribusi partikel komposit. Pengujian peforma fotokatalis menggunakan UV-Vis. CQDs yang disintesis memiliki ukuran partikel sebesar 6,62 nm. Hasil pengujian yang dilakukan tidak dapat memvalidasi terbentuknya CQDs sehingga diperlukan hasil pengujian TEM dan Spektroskopi Raman untuk mengetahui bahwa material yang terbentuk adalah CQDs. Komposit CuO/CQDs dengan penambahan massa CQDs 5%, 15%, 25%, dan 35% berhasil mendegradasi limbah methyelene blue selama satu jam dengan persen degradasi maksimal adalah 90,71% oleh komposit CuO/CQDs penambahan massa 25%.
============================================================
The textile industry is an industry that will continue to exist and develop along with the advancement of technology. One of the wastes that comes from this industry is textile dyes such as Methylene Blue. These compounds are toxic, carcinogenic, and cannot decompose naturally so they need to be treated before being disposed of in nature. On the other hand, cigarette butts are one of the most widely found garbage in the world. Cigarette butts are mostly made of cellulose acetate which can be synthesized into Carbon Quantum Dots (CQDs). CQDs are nanomaterials with low toxicity, stable photoluminescene, and flexible surface area. These nanomaterials can be applied in photocatalysts. CuO semiconductors have a small band gap of 1.2 – 2 eV. CQDs when composited with CuO can increase the surface area of CuO which can increase the photocatalyst. This research method focuses on the synthesis of CQDs from cigarette butts and photocatalysts using CuO/CQDs composites with the addition of 5%, 15%, 25%, and 35% CQDs masses with a total mass of 2 grams. The characterization tests used include XRD, FTIR, SEM/EDX, and PSA to analyze the structure, morphology, size, and distribution of composite particles. Photocatalyst performance testing using UV-Vis. The synthesized CQDs have a particle size of 6.62 nm. The results of the tests carried out could not validate the formation of CQDs, so the results of TEM and Raman Spectroscopy tests were needed to find out that the material formed was CQDs. CuO/CQDs composites with a mass addition of 5%, 15%, 25%, and 35% CQDs succeeded in degrading methyelene blue waste for one hour with a maximum degradation percentage of 90.71% by CuO/CQDs composites with a mass addition of 25%.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Cigarette Butts, CQDs, CuO, Methylene Blue, Photocatalysis, CQDs, CuO, Fotokatalisis, Methylene Blue, Puntung Rokok
Subjects:	Q Science > QD Chemistry > QD716 Photocatalysis.
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Josua Budiman Silaen
Date Deposited:	06 Aug 2024 00:56
Last Modified:	06 Aug 2024 00:56
URI:	http://repository.its.ac.id/id/eprint/110975

Actions (login required)

View Item