Sintesis Hidroksiapatit Dari Cangkang Keong Sawah Dengan Kombinasi Polycaprolactone (PCL) Sebagai Suture Anchor Berbasis 3D Printing

Rahmah, Annisa Alifia and Hidayatullah, Muhammad Alvin (2022) Sintesis Hidroksiapatit Dari Cangkang Keong Sawah Dengan Kombinasi Polycaprolactone (PCL) Sebagai Suture Anchor Berbasis 3D Printing. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 10411810000027-Undergraduate_Thesis.pdf - Accepted Version Download (3MB)

Abstract

Robekan pada rotator cuff merupakan salah satu cedera otot yang sering ditemui pada korban kecelakaan maupun atlet. Untuk mengobatinya, dalam dunia ortopedi sering digunakan Suture Anchor yang berfungsi untuk mengikat jaringan lunak ke implant yang tertanam di dalam tulang.. Salah satu bahan yang dapat digunakan sebahai bahan pembuatan suture anchor yaitu hidroksiapatit [Ca10(PO4)6(OH)2]. Hidroksiapatit (HAp) merupakan salah satu biokeramik kalsium fosfat yang memiliki kemiripan dengan mineral tulang sehingga dapat dimanfaatkan sebagai bahan pembuatan suture anchor. Salah satu metode sintesis hidroksiapatit yaitu Metode Presipitasi. Kalsium hidroksida (CaCO3) dapat diperoleh dari bahan alami, seperti Cangkang Keong Sawah. Namun HAP bersifat rapuh dan kekuatannya yang buruk, sehingga HAP biasanya dikombinasikan dengan polimer sebagai komposit untuk mengatasi keterbatasan sifat mekaniknya. Salah satu polimer yang dapat dimanfaatkan yaitu Polycaprolactone (PCL). Oleh sebab itu, perlu adanya penelitian lebih lanjut mengenai kombinasi pencampuran HAp dan (PCL) pada pembuatan filamen 3D Printing sebagai suture anchor. Variabel yang digunakan dalam penelitian ini yaitu rasio pencampuran HAp:PCL dalam membuat filamen dengan rasio pencampuran, yaitu 0,5:9,5 ; 1:9 ; 2:8. Untuk mengetahui pengaruh dari variabel yang telah ditentukan, dilakukan pengujian terhadap filamen 3D Printing. Pengujian yang dipilih yaitu dengan melakukan pengujian karakteristik hasil sintesis HAP, dan pengujian mekanik filamen 3D Printing. Nilai rasio perbandingan Ca/P yang didapatkan dalam senyawa hidroksiapatit sebesar 2,05. Nilai rasio ini didapatkan dari hasil pengujian SEM-EDX. Dari pengujian SEM juga didapatkan bentuk morfologi partikel yang berbentuk bulat, serta ukuran partikel sebesar 0,2 – 0,6 µm. Untuk hasil pengujian XRD didapatkan spektrum senyawa yang sesuai dengan spektrum hidroksiapatit standar (JCPDS No. 24-0033) dan untuk hasil pengujian FTIR yang telah dilakukan, didapatkan hasil yang mengindikasikan adanya kandungan hidroksiapatit pada sampel. Sedangkan hasil uji kuat tarik komposit yang paling optimal ketika pencampuran HAp:PCL dengan rasio 0,5:9,5.
===================================================================================================================================
A tear in the rotator cuff is one of the most common muscle injuries in accident victims and athletes. To treat it, in the world of orthopedics, Suture Anchor is often used which serves to bind soft tissue to implants embedded in bone. One of the materials that can be used as an anchor for making suture anchors is hydroxyapatite [Ca10(PO4)6(OH)2]. Hydroxyapatite (HAp) is a calcium phosphate bioceramic which has similarities with bone minerals so that it can be used as a material for making suture anchors. One of the hydroxyapatite synthesis methods is the Precipitation Method. Calcium hydroxide (CaCO3) can be obtained from natural materials, such as Sawah Snail Shells. However, HAP is brittle and has poor strength, so HAP is usually combined with polymers as composites to overcome the limitations of its mechanical properties. One of the polymers that can be used is Polycaprolactone (PCL). Therefore, there is a need for further research on the combination of mixing HAp and (PCL) in the manufacture of 3D Printing filaments as anchor sutures. The variables used in this study were the mixing ratio of HAp:PCL in making filaments with a mixing ratio of 0.5:9.5 ; 1:9 ; 2:8. To determine the effect of the variables that have been determined, the 3D Printing filament was tested. The chosen test is by testing the characteristics of the HAP synthesis results, and testing the mechanics of 3D Printing filaments. The value of the ratio of Ca/P obtained in the hydroxyapatite compound is 2.05. The value of this ratio is obtained from the results of the SEM-EDX test. From the SEM test, the morphological shape of the particles is spherical, and the particle size is 0.2 – 0.6 m. The XRD test results obtained a spectrum of compounds that matched the standard hydroxyapatite spectrum (JCPDS No. 24-0033) and for the results of the FTIR test that had been carried out, the results indicated the presence of hydroxyapatite content in the sample. While the results of the tensile strength test of the most optimal composite when mixing HAp:PCL with a ratio of 0.5: 9.5.

Item Type:	Thesis (Other)
Additional Information:	RSKI 660.297 Rah s-1 2022
Uncontrolled Keywords:	Rice Conch Shells, 3D Printing Filaments, Anchor Sutures, Hydroxyapatite, Polycaprolactone (PCL)
Subjects:	Q Science > QE Geology > QE391.A6 Hydroxyapatite
Divisions:	Faculty of Vocational > Industrial Chemical Engineering
Depositing User:	- Davi Wah
Date Deposited:	25 Sep 2024 08:59
Last Modified:	25 Sep 2024 08:59
URI:	http://repository.its.ac.id/id/eprint/115676