Pengaruh Gelatin Pada Gel Metil Selulosa/Gelatin Aqueous Mixture Terhadap Transmitansi Dan Gain Ultrasonik Untuk Aplikasi Kuplan Berbasis Air

Nada, Naufal Rais (2022) Pengaruh Gelatin Pada Gel Metil Selulosa/Gelatin Aqueous Mixture Terhadap Transmitansi Dan Gain Ultrasonik Untuk Aplikasi Kuplan Berbasis Air. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511840000047-Undergraduate_Thesis.pdf Download (4MB)

Abstract

Kuplan digunakan untuk mengisi ruang udara diantara transduser dan material uji agar suara dapat ditransmisikan ke dalam material uji dan tidak terpantulkan seluruhnya. Terdapat banyak jenis kuplan yang digunakan, salah satunya oli dan air, dimana keduanya memiliki impedansi akustik yang baik untuk digunakan sebagai kuplan, namun pada oli memiliki kekurangan pada kesulitan dalam pembersihannya dan air memiliki viskositas yang rendah sehingga sulit untuk melakukan pengujian vertikal dan overhead, namun air dapat dijadikan basis untuk membuat kuplan berbasis air. Metil selulosa digunakan sebagai bahan utama dan pengental, hal ini dikarenakan metil selulosa memiliki inhibitor yang baik dan juga merupakan inhibitor korosi yang baik, dan gelatin digunakan dikarenakan dapat meningkatkan kecepatan rambat. Penelitian ini bertujuan untuk menganalisis pengaruh konsentrasi Gelatin terhadap nilai transmitansi ultrasonik yang dihasilkan oleh masing-masing kuplan metil�selulosa berbasis air dengan berbagai variasi serta Menganalisis pengaruh konsentrasi Gelatin terhadap nilai gain yang dihasilkan pada pengujian ultrasonik dari masing-masing kuplan metil-selulosa berbasis air dengan berbagai variasi. Pada penelitian ini, metil selulosa dilarutkan dalam air pada magnetic stirrer dengan suhu 50oC, dan kecepatan 300RPM kemudian, gelatin diblooming dengan menaburkannya di atas mangkok yang berisi air yang kemudian dilarutkan pada larutan metil selulosa pada magnetic stirrer dengan suhu 50oC dan kecepatan 300 RPM selama 15 menit, dan kemudian didinginkan selama 60 menit. pada penelitian ini memvariasikan konsentrasi (wt%) metil selulosa:gelatin sebesar 4:0, 3,5:0,5, 3:1, 2,5:1,5, 2:2 dan dilakukan pengujian FTIR, Densitas, Cepat Rambat, Ultrasonik, dan perhitungan impedansi akustik dan koefisien transmisi. Hasil menunjukkan bahwa konsentrasi gelatin dapat memberikan pengaruh berupa peningkatan pada koefisien tranmistansinya dan penurunan nilai gain pada pengujian ultrasonik dengan variasi terbaik adalah variasi H2O/MC 2,0%/Gelatin 2,0% dengan nilai transmitansi sebesar 0,480 dan nilai gain sebesar 11,5 dB.
==============================================================================================================================
Couplant used to fill air space between tranducer and test material, so sound can be transmitted into the test material and all of them reflected. There are many type of couplants, some of them are oil and water, whereas the two of them have a good acoustic impedance that can be used between couplant, but oil is really difficult to clean and water have low viscosity so it's hard to do any test that need high viscosity, but water can be used to make a water-based couplant. Methyl cellulose was used as a main material and crosslinker, reasoning of this because methyl celullose solution has a big acoustic impedance than water and oil, also it is a good corossion inhibitor. Gelatin was used because it can be used to increase the ultrasound velocity. This research was done to analyze the effect of increasing the concentration of gelatin to ultrasonik transmittance that generated from each variation of methyl cellulose-gelatin water-based couplant and to analyze the effect of increasing the concentration of gelatin to gain that genereted from ultrasonik testing from each variation of methyl cellulose-gelatin water-based couplant. In this research, methyl cellulose was dissolved into water with magnetic stirrer in 50oC and 300 RPM speed, and the gelatin was bloomed in a bowl, after that the bloomed gelatin was dissolved into methyl cellulose in 50oC and 300 RPM speed for about 15 min, and cooled for about 60 min. This research variates concentration (wt%) of methyl cellulose:gelatin 4:0, 3,5:0,5, 3:1, 2,5:1,5, 2:2 and will be tested with FTIR, Density, Sound Propagation, Ultrasonik testing, and calculation of impedance acoustic and transmittance. Result showed that increasing the concentration of gelatin can increase transmittance and decrease gain in ultrasonik testing with the best variation is H2O/MC 2.0%/Gelatin 2,0% with transmittance value of 0.480 and gain value of 11,5 dB.

Item Type:	Thesis (Other)
Additional Information:	RSMt 620.28 Nad p-1 2022
Uncontrolled Keywords:	Gelatin, Kuplan, Metil Selulosa, Ultrasonik, Couplant, Gelatin, Methyl Cellulose, Ultrasonik
Subjects:	T Technology > T Technology (General) > TA404 Materials--Biodegradation
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	11 Dec 2024 07:00
Last Modified:	11 Dec 2024 07:00
URI:	http://repository.its.ac.id/id/eprint/115948

Actions (login required)

View Item