Pengaruh Gel Aloe Vera Pada Gel Metil Selulosa/Aloe Vera Aqueous Mixture Terhadap Transmitansi Dan Gain Ultrasonik Untuk Aplikasi Kuplan Berbasis Air

Kuncoro, Bagus Cahyo (2022) Pengaruh Gel Aloe Vera Pada Gel Metil Selulosa/Aloe Vera Aqueous Mixture Terhadap Transmitansi Dan Gain Ultrasonik Untuk Aplikasi Kuplan Berbasis Air. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511840000054-Undergraduate_Thesis.pdf Download (5MB)

Abstract

Pada uji ultrasonik, ketika transducer diaplikasikan langsung terhadap material uji tanpa adanya medium perantara akan menghasilkan refleksi gelombang suaraw. Penggunaan kuplan dapat menjadi solusi karena dapat menjadi media penghantar gelombang suara dari transducer ke material uji sehingga transducer dapat membaca gelombang suara yang dipantulkan. Air dapat digunakan sebagai kuplan, namun memiliki kekurangan terkait gain yang dihasilkan, viskositas dan kemampuan tahan korosi. Penelitian ini bertujuan untuk menganalisis pengaruh konsentrasi gel Aloe Vera terhadap transmitansi ultrasonik yang dihasilkan oleh masing-masing kuplan Metil Selulosa/Aloe Vera berbasis air serta menganalisis gain (sensitivitas) yang dihasilkan oleh masing-masing kuplan Metil Selulosa/Aloe Vera berbasis air. Dalam penelitian ini dilakukan pembuatan material kuplan Air/Metil Selulosa/Aloe Vera (H2O/MC/AV) dengan Metil Selulosa sebagai thickener/crosslinker dan Aloe Vera sebagai peningkat impedansi akustik. Metoe yang digunakan adalah gelasi (gelation). Dalam penelitian ini dianalisis pengaruh konsentrasi (%wt) Metil Selulosa dengan Aloe Vera adalah 4:0; 3:1; 2:2; 1:3; 0:4 terhadap transmitansi dan nilai gain yang dihasilkan pada pengujian ultrasonik. Pengujian yang dilakukan adalah FTIR, Visual, Densitas, Cepat Rambat Ultrasonik, dan Uji Ultrasonik. Hasil analisis menunjukkan kenaikkan konsentrasi Aloe Vera menurunkan transmitansi ultrasonik dengan nilai terendah adalah H20/MC0%/AV4% yaitu 0,3392 dan untuk nilai gain (sensitivitas) menunjukkan dengan kenaikkan konsentrasi Aloe Vera meningkatkan gain (sensitivitas) dengan nilai terbaik adalah H2O/MC4%/AV0% yaitu 13,5 dB.
==================================================================================================================================
In ultrasonic testing, when the transducer is applied directly to the test material without the presence of an intermediate medium, it will produce sound wave reflections. The use of a couplan can be a solution because it can be a medium for conducting sound waves from the transducer to the test material so that the transducer can read the reflected sound waves. Water can be used as a couplan, but has disadvantages related to the resulting gain, viscosity and corrosion resistance ability. This study aimed to analyze the effect of Aloe Vera gel concentration on the ultrasonic transmittance produced by each water-based Methyl Cellulose/Aloe Vera coupler and to analyze the gain (sensitivity) produced by each water-based Methyl Cellulose/Aloe Vera coupler. In this research, the material of Water/Methyl Cellulose/Aloe Vera (H2O/MC/AV) cuplan was made using Methyl Cellulose as a thickener/crosslinker and Aloe Vera as an acoustic impedance enhancer. The method used is gelation. In this study,the effect of concentration (%wt) of Methyl Cellulose with Aloe Vera was analyzed at 4:0; 3:1; 2:2; 1:3; 0:4 on the transmittance and gain value generated in ultrasonic testing. The tests carried out are FTIR, Visual, Density, Ultrasonic Speed Propace, and Ultrasonic Test. The results of the analysis show that increasing the concentration of Aloe Vera decreases ultrasonic transmittance with the lowest value being H2O/MC0%/AV4%, which is 0.3392 and for the gain value (sensitivity) it shows that increasing the concentration of Aloe Vera increases the gain (sensitivity) with the best value being H2O/MC4 %/AV0% ie 13.5 dB.

Item Type:	Thesis (Other)
Additional Information:	RSMt 620.112 74 Kun p-1, 2022
Uncontrolled Keywords:	Kuplan, Metil Selulosa, Aloe Vera, Couplant, Methyl Cellulose, Aloe Vera
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA418.16 Materials--Testing.
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	17 Dec 2024 02:59
Last Modified:	17 Dec 2024 02:59
URI:	http://repository.its.ac.id/id/eprint/115993

Actions (login required)

View Item