Analysis Of Pyrolysis Temperature Effect On Spent Bleaching Earth (SBE) Activation To ZnO/SBE Composite Materials Ability For Rhodamine B Degradatio

Arifa, Shafira Marelia (2022) Analysis Of Pyrolysis Temperature Effect On Spent Bleaching Earth (SBE) Activation To ZnO/SBE Composite Materials Ability For Rhodamine B Degradatio. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511840000115-Undergraduate_Thesis.pdf Download (7MB)

Abstract

Spent Bleaching Earth (SBE) merupakan limbah dari material penjernih dalam industri kelapa sawit yang dapat dimanfaatkan dalam pengolahan limbah bewarna seperti Rhodamine B. Namun, luas permukaan aktif pada SBE perlu ditingkan dengan aktivasi. Aktivasi pada SBE dapat dilakukan dengan metode pirolisis. Pirolisis digunakan agar luas permukaan SBE dan persentase degradasi Rhodamine B meningkat. Temperatur pirolisis menjadi faktor yang penting pada pembentukan pori-pori. Dalam proses pengolahan limbah, SBE hanya berlaku sebagai adsorben, yang belum efektif dalam mendegradasi limbah Rhodamine B, sehingga perlu dikompositkan dengan material semikonduktor ZnO sebagai material fotodegradasi. Tujuan dari penelitian ini yaitu menganalisis pengaruh temperatur pirolisis pada aktivasi material SBE terhadap morfologi dan struktur komposit ZnO/SBE dan kemampuan komposit ZnO/SBE untuk degradasi Rhodamine B. Metode penelitian ini adalah eksperimental, dimulai dari proses aktivasi SBE dengan metode pirolisis dan sintesis komposit ZnO/SBE dengan metode sol-gel. Variasi temperature pirolisis yang digunakan adalah 450, 500 dan 550 oC Pengujian yang dilakukan pada penelitian ini yaitu karakterisasi material yang terdiri dari uji XRD, FTIR, SEM-EDX, BET, dan Volatile Matter serta spektrofotometri UV-Vis dan GC-MS untuk pengujian fotokatalitik. Hasil menunjukkan bahwa material SBE dengan temperatur aktivasi 500 o C menunjukkan luas permukaan dan volume pori terbaik yaitu 106.851 m2 /g dan 0.119 cm3 /g. Morfologi permukaan komposit ZnO/SBE menunjukkan ZnO yang menempel pada permukaan SBE. Didapatkan hasil efisiensi degradasi komposit ZnO/SBE teraktivasi 450, 500 dan 550 oC, untuk waktu penyinaran selama 10 jam yaitu 42.34%, 67.8%, dan 48.69%.
=======================================================================================================================
Spent Bleaching Earth (SBE) is a waste of cleaning material in the palm oil industry that can be used to treat colored waste such as Rhodamine B. However, the active surface area of SBE needs to be increased by activation. Activation of SBE can be done by the pyrolysis method. Pyrolysis was used to increase the surface area of SBE and the percentage of Rhodamine B degradation. Pyrolysis temperature is an essential factor in the formation of pores. In the waste treatment process, SBE only acts as an adsorbent, which is not yet effective in degrading Rhodamine B waste, so it needs to be composited with ZnO semiconductor material as a photodegradation material. This study aimed to analyze the effect of pyrolysis temperature on the activation of SBE material on the morphology and structure of the ZnO/SBE composite and the ability of the ZnO/SBE composite to degrade Rhodamine B. This research method was experimental, starting from the activation process of SBE with the pyrolysis and synthesis of ZnO/SBE with the sol-gel method. The pyrolysis temperature variations used were 450, 500, and 550°C. The tests carried out in this study were material characterization consisting of XRD, FTIR, SEM-EDX, BET, and Volatile Matter tests as well as UV-Vis spectrophotometry and GC-MS for photocatalytic testing. . The results showed that the SBE material with an activation temperature of 500°C showed the best surface area and pore volume, namely 106,851 m2/g and 0.119 cm3/g. The surface morphology of the ZnO/SBE composite showed that ZnO adhered to the SBE surface. The results of the degradation efficiency of activated ZnO/SBE composites were 450, 500, and 550°C for 10 hours of irradiation time, namely 42.34%, 67.8%, and 48.69%

Item Type:	Thesis (Other)
Uncontrolled Keywords:	pirolisis, Rhodamine B, SBE, temperatur, ZnO, pyrolysis, Rhodamine B, SBE, temperature
Subjects:	T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL240.5 Composite materials
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	10 Feb 2025 07:17
Last Modified:	10 Feb 2025 07:17
URI:	http://repository.its.ac.id/id/eprint/118597

Actions (login required)

View Item