Analisis Pengaruh Temperatur Dan Kecepatan Screw Proses Ekstrusi Terhadap Sifat Reologi Dan Sifat Mekanik Feedstock Proyektil Frangible

Shafa, Mochamad Ichwan Al (2022) Analisis Pengaruh Temperatur Dan Kecepatan Screw Proses Ekstrusi Terhadap Sifat Reologi Dan Sifat Mekanik Feedstock Proyektil Frangible. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511840000140-Undergraduate_Thesis.pdf Download (20MB)

Abstract

Proses manufaktur proyektil frangible salah satunya dapat dilakukan dengan metode ekstrusi untuk membuat feedstock dan dilanjutkan dengan injection molding. Agar dapat digunakan sebagai proyektil frangible, feedstock perlu memiliki kekuatan tekan dan kekerasan yang sesuai. Selain itu, feedstock perlu memiliki nilai viskositas yang sesuai dengan yang dibutuhkan untuk proses injection molding. Pembuatan feedstock dilakukan dengan metode ekstrusi yang dimana pada proses tersebut terdapat beberapa parameter seperti kecepatan screw dan temperatur yang dapat mempengaruhi sifat feedstock hasil dari ekstrusi. Tujuan penelitian adalah untuk menganalisa pengaruh temperatur dan kecepatan screw ekstrusi terhadap sifat mekanik dan reologi feedstock. Feedstock dibuat menggunakan metode ekstrusi dengan variasi parameter temperatur 210-240, 220-250, 230-260 ℃ dan kecepatan screw 1,7; 1,9; dan 2,1 rpm. Feedstock hasil ekstrusi kemudian dilakukan pengujian tekan dan kekerasan untuk mengetahui sifat mekaniknya. Selain itu, juga dilakukan karakterisasi menggunakan Scanning Electron Microscopy (SEM) untuk mengetahui morfologinya. Lalu, akan dilakukan perhitungan viskositas untuk mengetahui pengaruh dari parameter yang digunakan. Dari hasil pengujian sifat mekanik yang dilakukan, diperoleh nilai kekuatan tekan dan kekerasan tertinggi oleh feedstock dengan variasi kecepatan screw 1,7 rpm dan temperatur 220-250 ℃ sebesar 137,5 MPa dan 80,43 HV. Tingginya nilai kekuatan tekan dan kekerasan yang didapat diperkirakan karena terbentuknya ikatan interlocking yang baik. Selain itu dapat dilihat juga perbedaan morfologi setiap variasi feedstock dari hasil pengujian Scanning Electrone Microscopy (SEM). Dapat diketahui juga, sifat mekanik feedstock bertambah seiring dengan bertambahnya kecepatan screw yang digunakan. Adapun perhitungan viskositas yang dihitung, terlihat bahwa viskositas semakin rendah seiring dengan tingginya temperatur yang digunakan pada proses
================================================================================================================================
One of the frangible projectile manufacturing processes can be done by extrusion method to make feedstock and followed by injection molding. In order to be used as a frangible projectile, the feedstock needs to have the appropriate compressive strength and hardness. In addition, the feedstock needs to have a viscosity value that matches that required for the injection molding process. The manufacture of feedstock is carried out by the extrusion method where in the process there are several parameters such as screw speed and temperature that can affect the nature of the feedstock resulting from extrusion. The purpose of this study was to analyze the effect of temperature and speed of the extrusion screw on the mechanical and rheological properties of the feedstock. Feedstock is made using the extrusion method with variations in temperature parameters 210-240, 220-250, 230-260 and screw speed 1.7; 1.9; and 2.1 rpm. The extruded feedstock is then subjected to compression and hardness tests to determine its mechanical properties. In addition, characterization was also carried out using Scanning Electron Microscopy (SEM) to determine the morphology. Then, a viscosity calculation will be carried out to determine the effect of the parameters used. From the results of the mechanical properties testing, the highest compressive strength and hardness values were obtained by the feedstock with variations in screw speed of 1.7 rpm and a temperature of 220-250 of 137.5 MPa and 80.43 HV. The high value of compressive strength and hardness obtained is thought to be due to the formation of a good interlocking bond. In addition, it can also be seen the morphological differences of each feedstock variation from the Scanning Electrone Microscopy (SEM) test results. It can also be seen that the mechanical properties of the feedstock increase with the increase in the screw speed used. As for the calculated viscosity calculation, it can be seen that the viscosity is getting lower along with the high temperature used in the process.

Item Type:	Thesis (Other)
Additional Information:	RSMt 671.732 Sha a-1 2022
Uncontrolled Keywords:	Komposit, Feedstock Cu/PA6, Sifat Mekanik, Viskositas, Composite, Feedstock Cu/PA6, Mechanical Properties, Viscosity
Subjects:	T Technology > TS Manufactures > TS670 Electroplating
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	11 Feb 2025 04:31
Last Modified:	11 Feb 2025 04:31
URI:	http://repository.its.ac.id/id/eprint/118638

Actions (login required)

View Item