Optimasi Tekanan Injeksi Dan Tekanan Holding Pada Proses Cetakan Injeksi Terhadap Perubahan Dimensi Dan Kebulatan Proyektil Komposit Stainless Steel 304L/PA6

Wibowo, Muhammad Rafii Pratama (2022) Optimasi Tekanan Injeksi Dan Tekanan Holding Pada Proses Cetakan Injeksi Terhadap Perubahan Dimensi Dan Kebulatan Proyektil Komposit Stainless Steel 304L/PA6. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02111840000061-Undergraduate Thesis.pdf Download (3MB)

Abstract

Proyektil frangible adalah proyektil yang mudah pecah menjadi serpihan kecil ketika mengenai target yang lebih keras agar mencegah terjadinya richochet dan backsplash. Pada pengembangannya, material frangible dapat diaplikasikan sebagai material proyektil. Pada penelitian ini, proyektil dibuat dengan proses cetakan injeksi berbahan komposit stainless steel 304L/PA6. Untuk memproduksi proyektil dengan toleransi yang tinggi, diperlukan optimasi parameter proses cetakan injeksi agar kecacatan pada produk dapat diminimalisir, khususnya perubahan dimensi dan kebulatan pada produk yang akan diteliti lebih lanjut. Penelitian diawali dengan pembuatan desain eksperimen parameter proses injeksi yang akan digunakan. Selanjutnya, parameter proses yang akan digunakan dalam eksperimen disimulasikan terlebih dulu pada software Autodesk Moldflow Adviser 2021 dilanjutkan eksperimen penentuan parameter injeksi untuk mendapatkan variabel proses dan konstan pada eksperimen. Setelah itu, eksperimen dilakukan menggunakan mesin cetakan injeksi. Proyektil yang dihasilkan kemudian diukur perubahan dimensi dan kebulatan pada bagian badan proyektil. Hasil pengukuran perubahan diameter dan kebulatan badan proyektil dilanjutkan pada tahap perhitungan optimasi parameter. Perhitungan optimasi parameter proses injeksi menggunakan metode Taguchi-Grey-Fuzzy untuk mengetahui parameter proses yang optimal, dilanjutkan dengan ANOVA menggunakan nilai grey-fuzzy reasoning grade atau GFRG untuk mengetahui kontribusi tiap parameter proses injeksi terhadap perubahan dimensi dan kebulatan proyektil. Selanjutnya, uji konfirmasi dilakukan untuk membuktikan nilai parameter injeksi hasil perhitungan optimasi merupakan variabel terbaik. Hasil dari penelitian ini yaitu tekanan injeksi dan tekanan holding berkontribusi terhadap perubahan dimensi dan kebulatan proyektil secara berurut sebesar 22,054% dan 21,113% dengan tekanan injeksi sebesar 9 MPa dan tekanan holding sebesar 9 MPa merupakan konfigurasi optimal. Berdasarkan uji hipotesis, tekanan injeksi dan tekanan holding tidak berpengaruh terhadap perubahan dimensi dan kebulatan
proyektil. Nilai GFRG dari uji konfirmasi berada di dalam interval keyakinan, sehingga hasil desain optimasi sesuai dengan hasil eksperimen
==================================================================================================================================
Frangible projectiles are projectiles that break easily into small pieces when hitting a harder target to prevent richochets and backsplashes. In its development, frangible materials can be applied as projectile materials. In this research, the projectiles were made by injection molding process made from stainless steel 304L/PA6 composite. To produce high tolerance projectiles, it is necessary to optimize the injection molding process parameters so that defects in the product can be minimized, especially dimensional change and roundness of the projectile which will be investigated further. The research begins with making an experimental design of the injection process parameters that will be used. Furthermore, the process parameters that will be used in the experiment will be simulated first on Autodesk Moldflow Adviser 2021 software to to obtain the process and constant variables for the experiment. After that, the projectile making experiment were carried out using an injection molding machine. The dimensional change and roundness of the projectile then measured on the body part. Then, the measurements of dimensional change and roundness of projectile on the experimental results are carried out to continue at the parameter optimization calculation stage. The calculation of the optimization of injection process parameters using the Taguchi-Grey-Fuzzy method to determine the optimal process parameters, followed by ANOVA using the value of gray-fuzzy reasoning grade or GFRG to determine the contribution of each injection process parameter toward the projectile dimensional change and roundness. Furthermore, confirmation experiments were carried out to prove the value of the injection parameter from the optimization calculation was the best variable. The result obtained that injection pressure and holding pressure contribute toward dimensional change and roundness of the projectile respectively by 22.054% and 21.113% with injection pressure of 9 MPa and holding pressure of 9 MPa is the optimum configuration. Based on the hypothesis test, injection pressure and holding pressure have no effect on dimensional changes and roundness of projectile. The GFRG value of the confirmation test is within the confidence interval, so the results of the optimization design are in accordance with the experimental results.

Item Type:	Thesis (Other)
Additional Information:	RSM 629.132 3 Sim i-1 2022
Uncontrolled Keywords:	Frangible Projectile, Injection Molding, Shrinkage, Dimensional Change, Roundness
Subjects:	T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL521 Aerodynamics, Hypersonic.
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	20 Feb 2025 02:50
Last Modified:	20 Feb 2025 02:50
URI:	http://repository.its.ac.id/id/eprint/118817

Actions (login required)

View Item