PENGARUH VARIASI TEKANAN GESEK,TEKANAN TEMPA DAN DURASI GESEK TERHADAP KEKUATAN IMPACT PADA SAMBUNGAN LAS GESEK (FRICTION WELDING) DENGAN MENGGUNAKAN BAJA PADUAN AISI 4140

SATYADIANTO, DICKY (2015) PENGARUH VARIASI TEKANAN GESEK,TEKANAN TEMPA DAN DURASI GESEK TERHADAP KEKUATAN IMPACT PADA SAMBUNGAN LAS GESEK (FRICTION WELDING) DENGAN MENGGUNAKAN BAJA PADUAN AISI 4140. Diploma thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
2109030058-Non_Degree.pdf - Published Version
Restricted to Repository staff only

Download (3MB) | Request a copy

Abstract

Pengelasan gesek adalah pengelasan solid-state tanpa menggunakan logam pengisi dengan menggunakan metode tekanan dimana dua benda kerja yang akan disambung ditempatkan dalam kontak dan diatur gerakan relatif dalam tekanan, maka gesekan akan membangkitkan panas disekitar permukaan kontak, ketika sudah mencapai temperatur tempa maka diberikan tekanan tempa. tetapi proses pengelasan ini pada dasarnya sangat dipengaruhi oleh kecepatan putaran, durasi gesekan dan tekanan aksial (gesek, tempa). Dalam penelitian ini dilakukan pengelasan gesek langsung. Proses yang dilakukan adalah dengan memvariasikan tekanan gesek sebesar 8 MPa, 14 MPa, dan 20 MPa dalam waktu gesekan 60 detik,80 detik, dan 100 detik sampai mencapai temperatur tertentu, kemudian diberikan variasi tekanan tempa sebesar 30 MPa, 40 MPa, 60 MPa dengan menggunakan baja AISI 4140 sebagai benda kerja, kecepatan putar yang digunakan 4500 Rpm. Efek dari tekanan gesek, tekanan tempa dan durasi gesekan terhadap impact strength dianalisa melalui uji impact. Dari penelitian ini didapat Kekuatan impact tertinggi diperoleh pada kombinasi parameter durasi gesek 100 detik, dengan tekanan gesek 20 MPa dan tekanan tempa 60 MPa yaitu sebesar 0,3228017 J/mm2. Kekuatan impact terendah diperoleh pada kombinasi parameter durasi gesek 60 detik, dengan tekanan gesek 8 MPa dan tekanan tempa 30 MPa yaitu sebesar 0,0420214 J/mm2. Perubahan tekanan gesekan, durasi gesek, dan tekanan tempa mempengaruhi temperatur pengelasan. Temperature Pengelasan tertinggi adalah 1075 oC. Dari ketiga parameter yang di variasikan, parameter tekanan gesek paling berpengaruh terhadap kekuatan impact sambungan las direct friction welding. ================================================================ Friction welding is solid-state welding without use filler with using a pressure method where two workpieces when will be joint is placed in contact and arranged by relative movement in pressure, hence friction will generating heat around surface of contact, when have reached forge temperature hence given pressure forge. But this welding process basically is very influenced by rotation speed, friction time and axial pressure (friction, forge). This research is done by direct-drive friction welding by made some variation with the parameters. Friction pressure is variated with 8 MPa, 14 MPa, and 20 Mpa, friction time is variated with 60 second, 80 second, and 100 second, then applied with forge pressure 30 MPa, 40 Mpa, and 60 Mpa using AISI 4140 Material in 4500 rpm. The effect of friction pressure, friction time, and forge pressure with impact strength analyzed with impact test. From the research we get maximum impact strength with 100 second of friction time, 20 Mpa of friction pressure, and 60 MPa of forge pressure is 0,3228017 J/mm2. Minimum impact strength is 0,0420214 J/mm2 with 60 second of friction time, 8 Mpa of friction pressure, and 30 MPa of forge friction. Variation of friction pressure, friction time, and forge pressure has a effect to welding temperature. Maximum welding temperature was 1075 oC. From the three parameter, friction pressure parameter have a biggest effect with impact strength in direct-contact friction welding.

Item Type: Thesis (Diploma)
Additional Information: RSM 671.52 Sat p
Uncontrolled Keywords: baja AISI 4140, kekuatan sambungan, durasi gesekan, tekanan gesek, tekanan tempa, pengelasan gesek langsung.
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Faculty of Industrial Technology > Mechanical Engineering > (D3) Diploma
Depositing User: Mrs Anis Wulandari
Date Deposited: 16 Jan 2017 03:03
Last Modified: 16 Jan 2017 03:03
URI: http://repository.its.ac.id/id/eprint/1591

Actions (login required)

View Item View Item