SATYADIANTO, DICKY (2015) PENGARUH VARIASI TEKANAN GESEK,TEKANAN TEMPA DAN DURASI GESEK TERHADAP KEKUATAN IMPACT PADA SAMBUNGAN LAS GESEK (FRICTION WELDING) DENGAN MENGGUNAKAN BAJA PADUAN AISI 4140. Diploma thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2109030058-Non_Degree.pdf - Published Version Download (3MB) | Preview |
Abstract
Pengelasan gesek adalah pengelasan solid-state tanpa
menggunakan logam pengisi dengan menggunakan metode
tekanan dimana dua benda kerja yang akan disambung
ditempatkan dalam kontak dan diatur gerakan relatif dalam
tekanan, maka gesekan akan membangkitkan panas disekitar
permukaan kontak, ketika sudah mencapai temperatur tempa
maka diberikan tekanan tempa. tetapi proses pengelasan ini pada
dasarnya sangat dipengaruhi oleh kecepatan putaran, durasi
gesekan dan tekanan aksial (gesek, tempa).
Dalam penelitian ini dilakukan pengelasan gesek
langsung. Proses yang dilakukan adalah dengan memvariasikan
tekanan gesek sebesar 8 MPa, 14 MPa, dan 20 MPa dalam waktu
gesekan 60 detik,80 detik, dan 100 detik sampai mencapai
temperatur tertentu, kemudian diberikan variasi tekanan tempa
sebesar 30 MPa, 40 MPa, 60 MPa dengan menggunakan baja
AISI 4140 sebagai benda kerja, kecepatan putar yang digunakan
4500 Rpm. Efek dari tekanan gesek, tekanan tempa dan durasi
gesekan terhadap impact strength dianalisa melalui uji impact.
Dari penelitian ini didapat Kekuatan impact tertinggi
diperoleh pada kombinasi parameter durasi gesek 100 detik,
dengan tekanan gesek 20 MPa dan tekanan tempa 60 MPa yaitu
sebesar 0,3228017 J/mm2. Kekuatan impact terendah diperoleh
pada kombinasi parameter durasi gesek 60 detik, dengan tekanan gesek 8 MPa dan tekanan tempa 30 MPa yaitu sebesar 0,0420214
J/mm2. Perubahan tekanan gesekan, durasi gesek, dan tekanan
tempa mempengaruhi temperatur pengelasan. Temperature
Pengelasan tertinggi adalah 1075 oC. Dari ketiga parameter
yang di variasikan, parameter tekanan gesek paling berpengaruh
terhadap kekuatan impact sambungan las direct friction welding.
================================================================
Friction welding is solid-state welding without use filler
with using a pressure method where two workpieces when will be
joint is placed in contact and arranged by relative movement in
pressure, hence friction will generating heat around surface of
contact, when have reached forge temperature hence given
pressure forge. But this welding process basically is very
influenced by rotation speed, friction time and axial pressure
(friction, forge).
This research is done by direct-drive friction welding by
made some variation with the parameters. Friction pressure is
variated with 8 MPa, 14 MPa, and 20 Mpa, friction time is
variated with 60 second, 80 second, and 100 second, then applied
with forge pressure 30 MPa, 40 Mpa, and 60 Mpa using AISI
4140 Material in 4500 rpm. The effect of friction pressure,
friction time, and forge pressure with impact strength analyzed
with impact test.
From the research we get maximum impact strength with
100 second of friction time, 20 Mpa of friction pressure, and 60
MPa of forge pressure is 0,3228017 J/mm2. Minimum impact
strength is 0,0420214 J/mm2 with 60 second of friction time, 8
Mpa of friction pressure, and 30 MPa of forge friction. Variation
of friction pressure, friction time, and forge pressure has a effect
to welding temperature. Maximum welding temperature was 1075
oC. From the three parameter, friction pressure parameter have a
biggest effect with impact strength in direct-contact friction
welding.
| Item Type: | Thesis (Diploma) |
|---|---|
| Additional Information: | RSM 671.52 Sat p |
| Uncontrolled Keywords: | baja AISI 4140, kekuatan sambungan, durasi gesekan, tekanan gesek, tekanan tempa, pengelasan gesek langsung. |
| Subjects: | T Technology > TJ Mechanical engineering and machinery |
| Divisions: | Faculty of Industrial Technology > Mechanical Engineering > 21401-(D3) Diploma 3 |
| Depositing User: | Anis Wulandari |
| Date Deposited: | 16 Jan 2017 03:03 |
| Last Modified: | 24 Aug 2018 06:41 |
| URI: | http://repository.its.ac.id/id/eprint/1591 |