Ramana, Adimas Bayu (2017) Pemanfaatan Fly Ash Dan Bottom Ash Pada Pembuatan Paving Geopolimer Dengan Mutu K-500 Untuk Skala Industri. Other thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
3114105044_Undergraduated_Thesis.pdf - Published Version Download (2MB) | Preview |
Abstract
Kondisi Sistem Ketenagalistrikan di Indonesia di dominasi oleh PLTU batubara sebesar 53,5%, pada tahun 2015 kebutuhan batubara sebesar 87,7 juta ton dan akan meningkat pada tahun 2019 sebesar 166,2 juta ton batubara karena sehubungan dengan adanya program 35000 MW. Limbah batubara yang dihasilkan dari pengopersian PLTU batubara berkisar 5% dari 166,2 juta ton yaitu 8,31 juta ton pada tahun 2019 (kementrian esdm, 2015). Berdasarkan observasi survei, Penimbunan pada limbah dari sisa pembakaran Batubara dalam 1 Ha maksimal 66900 ton akan tetapi dampak yang ditimbulkan banyak. Paving adalah salah satu alternatif bahan bangunan yang memiliki nilai positif. Dari segi pembuatan dan pelaksanaan juga sangat mudah.Dalam penelitian ini, fly ash dan bottom ash dimanfaatkan sebagai bahan dasar pembuatan paving geopolimer dengan campuran dari larutan alkali sebagai aktivatornya. Sehingga menemukan komposisi yang tepat mencapai K-500 dan diproduksi dalam skala industri. Perbandingan komposisi yang digunakan antara lain pasta dengan agregat adalah 30:70,agregat terdiri 34% pasir, 21% batu pecah, dan 13% abu batu ditambah bottom ash. Variasi bottom ash dengan abu batu adalah 80:20, Pasta terdiri dari 22,4% fly ash dan 9,6% larutan alkali , larutan alkali dari Na2SiO3 dan NaOH 8M adalah 1:1, serta penambahan air biasa untuk larutan alkali yang dipakai. Berdasarkan perhitungan analisa biaya paving geopolimer perbuah sebesar Rp. 1.095,-. Margin Harga Produksi Paving (HPP) GeoPav dengan Harga Jual Produsen lokal sebesar 52%. Didapatkan hasil bahwa paving geopolimer dengan penambahan bottom 80% dari berat volume abu batu memiliki kualitas baik. Berdasarkan SNI 03-0691-1996 tentang paving block dikategorikan paving mutu kelas A dikarenakan dalam nilai kuat tekan rata-rata besar 33,19 MPa, dalam nilai ketahanan aus rata-rata sebesar 0,080 mm/menit, dan dalam nilai resapan air rata-rata sebesar 3,43%.
==================================================================================================================
Conditions of Electricity System in Indonesia is dominated by coal power by 53.5%, in 2015 coal demand amounted to 87.7 million tons and will increase in 2019 amounted to 166.2 million tons of coal due in connection with the program of 35000 MW. Coal waste generated from coal power pengopersian about 5% of the 166.2 million tonnes of which 8.31 million tons in 2019 (Ministry of Energy, 2015). Based on the survey observations, stockpiling the waste from the combustion of coal in a 1 ha maximum of 66 900 tonnes but the impact many. Paving is one alternative building materials that have a positive value. In terms of manufacture and implementation is also very mudah.Dalam this study, fly ash and bottom ash is used as the base material paving geopolymer with a mixture of lye as an activator. So finding the right composition reaches K-500 and manufactured on an industrial scale. Comparison of composition used include pasta with an aggregate of 30: 70, the aggregate comprising 34% sand, 21% of crushed stone and stone plus 13% ash bottom ash. Variations bottom ash with stone dust is 80:20, Pasta consists of 22.4% and 9.6% fly ash lye, lye from Na2SiO3 and 8M NaOH is 1: 1, and the addition of ordinary water to lye used. Based on the calculation of the cost of paving geopolymer analysis apiece Rp. 1095, -. Paving Production Price Margin (HPP) GeoPav with Local Manufacturers Selling Price by 52%. RESULTS paving geopolymer with the addition of the bottom 80% of the weight of the volume of gray stone have good quality. SNI 03-0691-1996 based on paving block paving categorized quality class A because the value of the average compressive strength of 33.19 MPa great, the wear resistance value by an average of 0.080 mm / min, and the value of the average water infiltration of 3.43%.
Keywords: paving, geopolymer, fly ash, bottom ash, the analysis of costs, quality of paving blocks.
| Item Type: | Thesis (Other) |
|---|---|
| Uncontrolled Keywords: | paving, geopolimer, fly ash, bottom ash, analisa biaya, mutu paving block. |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials. |
| Divisions: | Faculty of Civil Engineering and Planning > Civil Engineering > 22201-(S1) Undergraduate Thesis |
| Depositing User: | - ADIMAS BAYU RAMANA |
| Date Deposited: | 03 Apr 2017 03:35 |
| Last Modified: | 17 Jul 2024 07:08 |
| URI: | http://repository.its.ac.id/id/eprint/2671 |
Actions (login required)
 |
View Item |