Pengaruh Penambahan Asam Adipat Terhadap Kekuatan Tarik Dan Stabilitas Termal Poliuretan

Dwijaya, Made Subekti (2016) Pengaruh Penambahan Asam Adipat Terhadap Kekuatan Tarik Dan Stabilitas Termal Poliuretan. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2709100008-Undergraduate-Theses.pdf

Download (6MB) | Preview

Abstract

Poliuretan adalah polimer dengan ciri khas adanya gugus uretan dalam rantai utama. Asam adipat, sebagai polyester poliol berfungsi untuk meningkatkan kekuatan tarik. Pada penelitian ini dilakukan variasi penambahan asam adipat untuk mengetahui pengaruhnya terhadap kekuatan tarik dan stabilitas termal poliuretan. Penambahan asam adipat dilakukan dengan komposisi 10, 20, 30, 40, 50, dan 60%wt. Resin epoksi dan penguatnya ditambahkan pada proses pencampuran. Campuran dituangkan kedalam cetakan spesimen uji tarik dan dilakukan proses curing selama 72 jam. Pengujian yang dilakukan adalah pengujian DSC/TGA, FTIR, pengujian kekerasan, dan pengujian tarik. Hasil dari pengujian DSC/TGA menunjukkan stabilitas termal tertinggi didapat pada spesimen 30% berat asam adipat dengan temperatur degradasi 5% pada 203.167oC. Pengujian FTIR memberikan hasil terdapatnya gugus pembentuk poliuretan. Pengujian kekerasan menunjukkan kekerasan tertinggi didapat dari spesimen 40% berat asam adipat dengan nilai kekerasan 89 shore A. Hasil pengujian tarik memberikan hasil nilai kekuatan tarik tertinggi didapat dari spesimen 40% berat asam adipat sebesar 3.029554655 MPa. ================================================================================== Polyurethane is polymer characterized by urethane group on the main link. Adipic acid, as the polyester polyol, is used to increase the tensile strength. In this research, adipic acid was added with varying composition of 10, 20, 30, 40, 50, and 60%wt. Epoxy resin & hardener were added when the mixing process. The mixture poured into tensile test cast and cured for 72 hour in room temperature. Characterized being conducted in this research were DSC/TGA,FTIR, hardness test, and tensile test. The result of DSC/TGA shows highest thermal stability achieve with 30%wt adipic acid addition with 5% thermal degradation on 203.167oC. FTIR test shows the forming of Urethane group . Hardness test shows highest hardness number 89 shore A when the speciment contain 40%wt adipic acid . Tensile test shows highest tensile strength on 3.029554655 MPa when the speciment contain 40%wt adipic acid.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.194 92 Dwi p
Uncontrolled Keywords: Poliuretan, Asam Adipat, Epoxy Resin, Polyurethane, Adipic Acid
Subjects: T Technology > T Technology (General)
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > (S1) Undergraduate Theses
Depositing User: Mrs Anis Wulandari
Date Deposited: 07 Jul 2017 05:39
Last Modified: 26 Dec 2018 07:20
URI: http://repository.its.ac.id/id/eprint/41908

Actions (login required)

View Item View Item